EN 1.4416 Stainless Steel vs. EN 1.0601 Steel
Both EN 1.4416 stainless steel and EN 1.0601 steel are iron alloys. They have 50% of their average alloy composition in common. There are 30 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is EN 1.4416 stainless steel and the bottom bar is EN 1.0601 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 150 | |
| 210 |
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Elongation at Break, % | 34 | |
| 11 |
| Fatigue Strength, MPa | 170 | |
| 220 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 79 | |
| 72 |
| Tensile Strength: Ultimate (UTS), MPa | 500 | |
| 730 |
| Tensile Strength: Yield (Proof), MPa | 210 | |
| 350 |
Thermal Properties
| Latent Heat of Fusion, J/g | 300 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 1100 | |
| 400 |
| Melting Completion (Liquidus), °C | 1450 | |
| 1460 |
| Melting Onset (Solidus), °C | 1400 | |
| 1410 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 12 | |
| 48 |
| Thermal Expansion, µm/m-K | 15 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 1.7 | |
| 7.2 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 1.9 | |
| 8.3 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 31 | |
| 2.1 |
| Density, g/cm3 | 8.1 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 5.8 | |
| 1.5 |
| Embodied Energy, MJ/kg | 79 | |
| 19 |
| Embodied Water, L/kg | 190 | |
| 47 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 140 | |
| 65 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 110 | |
| 330 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 24 |
| Strength to Weight: Axial, points | 17 | |
| 26 |
| Strength to Weight: Bending, points | 17 | |
| 23 |
| Thermal Diffusivity, mm2/s | 3.2 | |
| 13 |
| Thermal Shock Resistance, points | 12 | |
| 23 |
Alloy Composition
| Carbon (C), % | 0 to 0.030 | |
| 0.57 to 0.65 |
| Chromium (Cr), % | 19 to 21 | |
| 0 to 0.4 |
| Iron (Fe), % | 45.2 to 52.4 | |
| 97.1 to 98.8 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0.6 to 0.9 |
| Molybdenum (Mo), % | 4.5 to 5.5 | |
| 0 to 0.1 |
| Nickel (Ni), % | 24 to 26 | |
| 0 to 0.4 |
| Nitrogen (N), % | 0.12 to 0.2 | |
| 0 |
| Phosphorus (P), % | 0 to 0.035 | |
| 0 to 0.045 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 0.4 |
| Sulfur (S), % | 0 to 0.020 | |
| 0 to 0.045 |