EN 1.4417 Stainless Steel vs. EN 1.7202 Steel
Both EN 1.4417 stainless steel and EN 1.7202 steel are iron alloys. They have 64% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is EN 1.4417 stainless steel and the bottom bar is EN 1.7202 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Poisson's Ratio | 0.27 | |
| 0.29 |
| Shear Modulus, GPa | 81 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 730 | |
| 530 to 1810 |
Thermal Properties
| Latent Heat of Fusion, J/g | 300 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 1100 | |
| 420 |
| Melting Completion (Liquidus), °C | 1450 | |
| 1460 |
| Melting Onset (Solidus), °C | 1410 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 470 |
| Thermal Conductivity, W/m-K | 17 | |
| 46 |
| Thermal Expansion, µm/m-K | 13 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.2 | |
| 7.3 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.5 | |
| 8.4 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 21 | |
| 2.5 |
| Density, g/cm3 | 7.9 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 4.1 | |
| 1.5 |
| Embodied Energy, MJ/kg | 57 | |
| 20 |
| Embodied Water, L/kg | 180 | |
| 51 |
Common Calculations
| Stiffness to Weight: Axial, points | 15 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 |
| Strength to Weight: Axial, points | 26 | |
| 19 to 64 |
| Strength to Weight: Bending, points | 23 | |
| 19 to 42 |
| Thermal Diffusivity, mm2/s | 4.6 | |
| 12 |
| Thermal Shock Resistance, points | 20 | |
| 16 to 53 |
Alloy Composition
| Carbon (C), % | 0 to 0.030 | |
| 0.35 to 0.4 |
| Chromium (Cr), % | 24 to 26 | |
| 0.9 to 1.2 |
| Copper (Cu), % | 0 to 1.0 | |
| 0 to 0.25 |
| Iron (Fe), % | 56.7 to 66.9 | |
| 96.6 to 98 |
| Manganese (Mn), % | 0 to 1.5 | |
| 0.6 to 0.9 |
| Molybdenum (Mo), % | 3.0 to 4.0 | |
| 0.15 to 0.3 |
| Nickel (Ni), % | 6.0 to 8.5 | |
| 0 |
| Nitrogen (N), % | 0.15 to 0.25 | |
| 0 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 0.3 |
| Sulfur (S), % | 0 to 0.020 | |
| 0 to 0.025 |
| Tungsten (W), % | 0 to 1.0 | |
| 0 |