EN 1.4419 Stainless Steel vs. ACI-ASTM CD6MN Steel

Both EN 1.4419 stainless steel and ACI-ASTM CD6MN steel are iron alloys. They have 82% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is EN 1.4419 stainless steel and the bottom bar is ACI-ASTM CD6MN steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 11 to 17
28
Fatigue Strength, MPa 230 to 680
370
Poisson's Ratio 0.28
0.27
Shear Modulus, GPa 76
80
Tensile Strength: Ultimate (UTS), MPa 660 to 1590
730
Tensile Strength: Yield (Proof), MPa 370 to 1240
510

Thermal Properties

Latent Heat of Fusion, J/g 280
300
Maximum Temperature: Corrosion, °C 390
450
Maximum Temperature: Mechanical, °C 790
1100
Melting Completion (Liquidus), °C 1440
1440
Melting Onset (Solidus), °C 1400
1390
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 30
16
Thermal Expansion, µm/m-K 11
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.8
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 3.2
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 8.0
17
Density, g/cm3 7.7
7.7
Embodied Carbon, kg CO2/kg material 2.2
3.4
Embodied Energy, MJ/kg 30
48
Embodied Water, L/kg 110
170

Common Calculations

PREN (Pitting Resistance) 16
36
Resilience: Ultimate (Unit Rupture Work), MJ/m3 95 to 170
180
Resilience: Unit (Modulus of Resilience), kJ/m3 350 to 3920
650
Stiffness to Weight: Axial, points 14
15
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 24 to 57
26
Strength to Weight: Bending, points 22 to 39
23
Thermal Diffusivity, mm2/s 8.1
4.4
Thermal Shock Resistance, points 23 to 55
20

Alloy Composition

Carbon (C), % 0.36 to 0.42
0 to 0.060
Chromium (Cr), % 13 to 14.5
24 to 27
Iron (Fe), % 82 to 86
62.1 to 70.1
Manganese (Mn), % 0 to 1.0
0 to 1.0
Molybdenum (Mo), % 0.6 to 1.0
1.8 to 2.5
Nickel (Ni), % 0
4.0 to 6.0
Nitrogen (N), % 0
0.15 to 0.25
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.015
0 to 0.040