MakeItFrom.com
Menu (ESC)

EN 1.4419 Stainless Steel vs. AWS E70C-Ni2

Both EN 1.4419 stainless steel and AWS E70C-Ni2 are iron alloys. They have 85% of their average alloy composition in common. There are 27 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is EN 1.4419 stainless steel and the bottom bar is AWS E70C-Ni2.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 11 to 17
27
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
72
Tensile Strength: Ultimate (UTS), MPa 660 to 1590
560
Tensile Strength: Yield (Proof), MPa 370 to 1240
450

Thermal Properties

Latent Heat of Fusion, J/g 280
250
Melting Completion (Liquidus), °C 1440
1450
Melting Onset (Solidus), °C 1400
1410
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 30
52
Thermal Expansion, µm/m-K 11
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.8
7.5
Electrical Conductivity: Equal Weight (Specific), % IACS 3.2
8.6

Otherwise Unclassified Properties

Base Metal Price, % relative 8.0
3.3
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 2.2
1.6
Embodied Energy, MJ/kg 30
22
Embodied Water, L/kg 110
51

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 95 to 170
140
Resilience: Unit (Modulus of Resilience), kJ/m3 350 to 3920
540
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 24 to 57
20
Strength to Weight: Bending, points 22 to 39
19
Thermal Diffusivity, mm2/s 8.1
14
Thermal Shock Resistance, points 23 to 55
17

Alloy Composition

Carbon (C), % 0.36 to 0.42
0 to 0.080
Chromium (Cr), % 13 to 14.5
0
Copper (Cu), % 0
0 to 0.35
Iron (Fe), % 82 to 86
94.1 to 98.3
Manganese (Mn), % 0 to 1.0
0 to 1.3
Molybdenum (Mo), % 0.6 to 1.0
0
Nickel (Ni), % 0
1.8 to 2.8
Phosphorus (P), % 0 to 0.040
0 to 0.025
Silicon (Si), % 0 to 1.0
0 to 0.9
Sulfur (S), % 0 to 0.015
0 to 0.030
Vanadium (V), % 0
0 to 0.030
Residuals, % 0
0 to 0.5