EN 1.4419 Stainless Steel vs. EN 1.5418 Steel

Both EN 1.4419 stainless steel and EN 1.5418 steel are iron alloys. They have 85% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is EN 1.4419 stainless steel and the bottom bar is EN 1.5418 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 76
73
Tensile Strength: Ultimate (UTS), MPa 660 to 1590
490 to 1780

Thermal Properties

Latent Heat of Fusion, J/g 280
250
Maximum Temperature: Mechanical, °C 790
400
Melting Completion (Liquidus), °C 1440
1460
Melting Onset (Solidus), °C 1400
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 30
48
Thermal Expansion, µm/m-K 11
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.8
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 3.2
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 8.0
2.1
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 2.2
1.5
Embodied Energy, MJ/kg 30
19
Embodied Water, L/kg 110
47

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 24 to 57
17 to 63
Strength to Weight: Bending, points 22 to 39
18 to 42
Thermal Diffusivity, mm2/s 8.1
13
Thermal Shock Resistance, points 23 to 55
14 to 53

Alloy Composition

Carbon (C), % 0.36 to 0.42
0.35 to 0.4
Chromium (Cr), % 13 to 14.5
0
Copper (Cu), % 0
0 to 0.25
Iron (Fe), % 82 to 86
97.8 to 98.9
Manganese (Mn), % 0 to 1.0
0.6 to 0.9
Molybdenum (Mo), % 0.6 to 1.0
0.2 to 0.3
Phosphorus (P), % 0 to 0.040
0 to 0.025
Silicon (Si), % 0 to 1.0
0 to 0.3
Sulfur (S), % 0 to 0.015
0 to 0.025