EN 1.4421 Stainless Steel vs. ASTM A266 Carbon Steel
Both EN 1.4421 stainless steel and ASTM A266 carbon steel are iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.
For each property being compared, the top bar is EN 1.4421 stainless steel and the bottom bar is ASTM A266 carbon steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Elongation at Break, % | 11 to 17 | |
| 21 to 26 |
| Fatigue Strength, MPa | 380 to 520 | |
| 170 to 200 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 77 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 880 to 1100 | |
| 500 to 600 |
| Tensile Strength: Yield (Proof), MPa | 620 to 950 | |
| 230 to 290 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 870 | |
| 400 |
| Melting Completion (Liquidus), °C | 1440 | |
| 1460 |
| Melting Onset (Solidus), °C | 1400 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 470 |
| Thermal Conductivity, W/m-K | 16 | |
| 51 to 52 |
| Thermal Expansion, µm/m-K | 10 | |
| 12 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.2 | |
| 7.1 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.5 | |
| 8.1 to 8.2 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 12 | |
| 1.8 |
| Density, g/cm3 | 7.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 2.6 | |
| 1.4 |
| Embodied Energy, MJ/kg | 36 | |
| 18 to 19 |
| Embodied Water, L/kg | 130 | |
| 46 to 47 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 120 to 140 | |
| 110 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 960 to 2270 | |
| 140 to 230 |
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 |
| Strength to Weight: Axial, points | 31 to 39 | |
| 18 to 21 |
| Strength to Weight: Bending, points | 26 to 30 | |
| 18 to 20 |
| Thermal Diffusivity, mm2/s | 4.4 | |
| 14 |
| Thermal Shock Resistance, points | 31 to 39 | |
| 16 to 19 |