EN 1.4421 Stainless Steel vs. EN 1.4903 Stainless Steel

Both EN 1.4421 stainless steel and EN 1.4903 stainless steel are iron alloys. They have 88% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is EN 1.4421 stainless steel and the bottom bar is EN 1.4903 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 11 to 17
20 to 21
Fatigue Strength, MPa 380 to 520
320 to 330
Impact Strength: V-Notched Charpy, J 30 to 67
42 to 46
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
75
Tensile Strength: Ultimate (UTS), MPa 880 to 1100
670 to 680
Tensile Strength: Yield (Proof), MPa 620 to 950
500

Thermal Properties

Latent Heat of Fusion, J/g 280
270
Maximum Temperature: Corrosion, °C 410
380
Maximum Temperature: Mechanical, °C 870
650
Melting Completion (Liquidus), °C 1440
1460
Melting Onset (Solidus), °C 1400
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 16
26
Thermal Expansion, µm/m-K 10
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
3.4
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
4.0

Otherwise Unclassified Properties

Base Metal Price, % relative 12
7.0
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 2.6
2.6
Embodied Energy, MJ/kg 36
36
Embodied Water, L/kg 130
88

Common Calculations

PREN (Pitting Resistance) 18
13
Resilience: Ultimate (Unit Rupture Work), MJ/m3 120 to 140
120 to 130
Resilience: Unit (Modulus of Resilience), kJ/m3 960 to 2270
650
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 31 to 39
24
Strength to Weight: Bending, points 26 to 30
22
Thermal Diffusivity, mm2/s 4.4
7.0
Thermal Shock Resistance, points 31 to 39
23

Alloy Composition

Aluminum (Al), % 0
0 to 0.040
Carbon (C), % 0 to 0.060
0.080 to 0.12
Chromium (Cr), % 15.5 to 17.5
8.0 to 9.5
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 74.4 to 80.5
87.1 to 90.5
Manganese (Mn), % 0 to 1.0
0.3 to 0.6
Molybdenum (Mo), % 0 to 0.7
0.85 to 1.1
Nickel (Ni), % 4.0 to 5.5
0 to 0.4
Niobium (Nb), % 0
0.060 to 0.1
Nitrogen (N), % 0
0.030 to 0.070
Phosphorus (P), % 0 to 0.035
0 to 0.025
Silicon (Si), % 0 to 0.8
0 to 0.5
Sulfur (S), % 0 to 0.020
0 to 0.015
Vanadium (V), % 0
0.18 to 0.25