EN 1.4421 Stainless Steel vs. N06230 Nickel
EN 1.4421 stainless steel belongs to the iron alloys classification, while N06230 nickel belongs to the nickel alloys. They have a modest 24% of their average alloy composition in common, which, by itself, doesn't mean much. There are 29 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.
For each property being compared, the top bar is EN 1.4421 stainless steel and the bottom bar is N06230 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 210 |
| Elongation at Break, % | 11 to 17 | |
| 38 to 48 |
| Fatigue Strength, MPa | 380 to 520 | |
| 250 to 360 |
| Poisson's Ratio | 0.28 | |
| 0.28 |
| Shear Modulus, GPa | 77 | |
| 83 |
| Tensile Strength: Ultimate (UTS), MPa | 880 to 1100 | |
| 620 to 840 |
| Tensile Strength: Yield (Proof), MPa | 620 to 950 | |
| 330 to 400 |
Thermal Properties
| Latent Heat of Fusion, J/g | 280 | |
| 310 |
| Maximum Temperature: Mechanical, °C | 870 | |
| 990 |
| Melting Completion (Liquidus), °C | 1440 | |
| 1370 |
| Melting Onset (Solidus), °C | 1400 | |
| 1300 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 420 |
| Thermal Conductivity, W/m-K | 16 | |
| 8.9 |
| Thermal Expansion, µm/m-K | 10 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.2 | |
| 1.4 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.5 | |
| 1.3 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 12 | |
| 85 |
| Density, g/cm3 | 7.8 | |
| 9.5 |
| Embodied Carbon, kg CO2/kg material | 2.6 | |
| 11 |
| Embodied Energy, MJ/kg | 36 | |
| 160 |
| Embodied Water, L/kg | 130 | |
| 290 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 120 to 140 | |
| 200 to 330 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 960 to 2270 | |
| 250 to 380 |
| Stiffness to Weight: Axial, points | 14 | |
| 12 |
| Stiffness to Weight: Bending, points | 25 | |
| 21 |
| Strength to Weight: Axial, points | 31 to 39 | |
| 18 to 25 |
| Strength to Weight: Bending, points | 26 to 30 | |
| 17 to 21 |
| Thermal Diffusivity, mm2/s | 4.4 | |
| 2.3 |
| Thermal Shock Resistance, points | 31 to 39 | |
| 17 to 23 |
Alloy Composition
| Aluminum (Al), % | 0 | |
| 0.2 to 0.5 |
| Boron (B), % | 0 | |
| 0 to 0.015 |
| Carbon (C), % | 0 to 0.060 | |
| 0.050 to 0.15 |
| Chromium (Cr), % | 15.5 to 17.5 | |
| 20 to 24 |
| Cobalt (Co), % | 0 | |
| 0 to 5.0 |
| Iron (Fe), % | 74.4 to 80.5 | |
| 0 to 3.0 |
| Lanthanum (La), % | 0 | |
| 0.0050 to 0.050 |
| Manganese (Mn), % | 0 to 1.0 | |
| 0.3 to 1.0 |
| Molybdenum (Mo), % | 0 to 0.7 | |
| 1.0 to 3.0 |
| Nickel (Ni), % | 4.0 to 5.5 | |
| 47.5 to 65.2 |
| Phosphorus (P), % | 0 to 0.035 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 to 0.8 | |
| 0.25 to 0.75 |
| Sulfur (S), % | 0 to 0.020 | |
| 0 to 0.015 |
| Tungsten (W), % | 0 | |
| 13 to 15 |