EN 1.4422 Stainless Steel vs. N08925 Stainless Steel

Both EN 1.4422 stainless steel and N08925 stainless steel are iron alloys. They have 66% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is EN 1.4422 stainless steel and the bottom bar is N08925 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 17
45
Fatigue Strength, MPa 380
310
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
80
Shear Strength, MPa 520
470
Tensile Strength: Ultimate (UTS), MPa 850
680
Tensile Strength: Yield (Proof), MPa 630
340

Thermal Properties

Latent Heat of Fusion, J/g 270
300
Maximum Temperature: Corrosion, °C 390
420
Maximum Temperature: Mechanical, °C 760
1100
Melting Completion (Liquidus), °C 1450
1460
Melting Onset (Solidus), °C 1410
1410
Specific Heat Capacity, J/kg-K 470
460
Thermal Conductivity, W/m-K 16
13
Thermal Expansion, µm/m-K 10
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.3
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 2.6
1.9

Otherwise Unclassified Properties

Base Metal Price, % relative 11
33
Density, g/cm3 7.9
8.1
Embodied Carbon, kg CO2/kg material 2.7
6.2
Embodied Energy, MJ/kg 37
84
Embodied Water, L/kg 110
200

Common Calculations

PREN (Pitting Resistance) 17
44
Resilience: Ultimate (Unit Rupture Work), MJ/m3 130
250
Resilience: Unit (Modulus of Resilience), kJ/m3 1000
280
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 30
23
Strength to Weight: Bending, points 25
21
Thermal Diffusivity, mm2/s 4.3
3.5
Thermal Shock Resistance, points 31
15

Alloy Composition

Carbon (C), % 0 to 0.020
0 to 0.020
Chromium (Cr), % 11 to 13
19 to 21
Copper (Cu), % 0.2 to 0.8
0.8 to 1.5
Iron (Fe), % 76.8 to 83.5
42.7 to 50.1
Manganese (Mn), % 0 to 2.0
0 to 1.0
Molybdenum (Mo), % 1.3 to 1.8
6.0 to 7.0
Nickel (Ni), % 4.0 to 5.0
24 to 26
Nitrogen (N), % 0 to 0.020
0.1 to 0.2
Phosphorus (P), % 0 to 0.040
0 to 0.045
Silicon (Si), % 0 to 0.5
0 to 0.5
Sulfur (S), % 0 to 0.0030
0 to 0.030