EN 1.4422 Stainless Steel vs. S31060 Stainless Steel

Both EN 1.4422 stainless steel and S31060 stainless steel are iron alloys. They have 82% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4422 stainless steel and the bottom bar is S31060 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 17
46
Fatigue Strength, MPa 380
290
Poisson's Ratio 0.28
0.27
Shear Modulus, GPa 76
78
Shear Strength, MPa 520
480
Tensile Strength: Ultimate (UTS), MPa 850
680
Tensile Strength: Yield (Proof), MPa 630
310

Thermal Properties

Latent Heat of Fusion, J/g 270
290
Maximum Temperature: Corrosion, °C 390
440
Maximum Temperature: Mechanical, °C 760
1080
Melting Completion (Liquidus), °C 1450
1420
Melting Onset (Solidus), °C 1410
1370
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 16
15
Thermal Expansion, µm/m-K 10
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.3
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 2.6
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 11
18
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 2.7
3.4
Embodied Energy, MJ/kg 37
48
Embodied Water, L/kg 110
170

Common Calculations

PREN (Pitting Resistance) 17
26
Resilience: Ultimate (Unit Rupture Work), MJ/m3 130
260
Resilience: Unit (Modulus of Resilience), kJ/m3 1000
250
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 30
24
Strength to Weight: Bending, points 25
22
Thermal Diffusivity, mm2/s 4.3
4.0
Thermal Shock Resistance, points 31
15

Alloy Composition

Boron (B), % 0
0.0010 to 0.010
Carbon (C), % 0 to 0.020
0.050 to 0.1
Cerium (Ce), % 0
0 to 0.070
Chromium (Cr), % 11 to 13
22 to 24
Copper (Cu), % 0.2 to 0.8
0
Iron (Fe), % 76.8 to 83.5
61.4 to 67.8
Lanthanum (La), % 0
0 to 0.070
Manganese (Mn), % 0 to 2.0
0 to 1.0
Molybdenum (Mo), % 1.3 to 1.8
0
Nickel (Ni), % 4.0 to 5.0
10 to 12.5
Nitrogen (N), % 0 to 0.020
0.18 to 0.25
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 0.5
0 to 0.5
Sulfur (S), % 0 to 0.0030
0 to 0.030