EN 1.4422 Stainless Steel vs. S38100 Stainless Steel

Both EN 1.4422 stainless steel and S38100 stainless steel are iron alloys. They have 79% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4422 stainless steel and the bottom bar is S38100 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 17
45
Fatigue Strength, MPa 380
210
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 76
76
Shear Strength, MPa 520
400
Tensile Strength: Ultimate (UTS), MPa 850
580
Tensile Strength: Yield (Proof), MPa 630
230

Thermal Properties

Latent Heat of Fusion, J/g 270
320
Maximum Temperature: Corrosion, °C 390
410
Maximum Temperature: Mechanical, °C 760
970
Melting Completion (Liquidus), °C 1450
1400
Melting Onset (Solidus), °C 1410
1350
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 16
15
Thermal Expansion, µm/m-K 10
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.3
2.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.6
2.6

Otherwise Unclassified Properties

Base Metal Price, % relative 11
20
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 2.7
3.8
Embodied Energy, MJ/kg 37
54
Embodied Water, L/kg 110
160

Common Calculations

PREN (Pitting Resistance) 17
18
Resilience: Ultimate (Unit Rupture Work), MJ/m3 130
210
Resilience: Unit (Modulus of Resilience), kJ/m3 1000
140
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 30
21
Strength to Weight: Bending, points 25
20
Thermal Diffusivity, mm2/s 4.3
4.0
Thermal Shock Resistance, points 31
13

Alloy Composition

Carbon (C), % 0 to 0.020
0 to 0.080
Chromium (Cr), % 11 to 13
17 to 19
Copper (Cu), % 0.2 to 0.8
0
Iron (Fe), % 76.8 to 83.5
57.9 to 64
Manganese (Mn), % 0 to 2.0
0 to 2.0
Molybdenum (Mo), % 1.3 to 1.8
0
Nickel (Ni), % 4.0 to 5.0
17.5 to 18.5
Nitrogen (N), % 0 to 0.020
0
Phosphorus (P), % 0 to 0.040
0 to 0.030
Silicon (Si), % 0 to 0.5
1.5 to 2.5
Sulfur (S), % 0 to 0.0030
0 to 0.030