EN 1.4432 Stainless Steel vs. EN 1.4864 Stainless Steel

Both EN 1.4432 stainless steel and EN 1.4864 stainless steel are iron alloys. Both are furnished in the solution annealed (AT) condition. They have 76% of their average alloy composition in common. There are 33 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is EN 1.4432 stainless steel and the bottom bar is EN 1.4864 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
190
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 44
33
Fatigue Strength, MPa 220
200
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 78
75
Shear Strength, MPa 420
430
Tensile Strength: Ultimate (UTS), MPa 610
650
Tensile Strength: Yield (Proof), MPa 250
260

Thermal Properties

Latent Heat of Fusion, J/g 290
310
Maximum Temperature: Corrosion, °C 410
410
Maximum Temperature: Mechanical, °C 960
1100
Melting Completion (Liquidus), °C 1450
1390
Melting Onset (Solidus), °C 1400
1340
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 15
13
Thermal Expansion, µm/m-K 16
14

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.3
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 2.6
1.9

Otherwise Unclassified Properties

Base Metal Price, % relative 19
30
Density, g/cm3 7.9
8.0
Embodied Carbon, kg CO2/kg material 3.9
5.3
Embodied Energy, MJ/kg 54
75
Embodied Water, L/kg 150
180

Common Calculations

PREN (Pitting Resistance) 27
17
Resilience: Ultimate (Unit Rupture Work), MJ/m3 220
170
Resilience: Unit (Modulus of Resilience), kJ/m3 150
170
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 21
23
Strength to Weight: Bending, points 20
21
Thermal Diffusivity, mm2/s 4.0
3.3
Thermal Shock Resistance, points 14
17

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.15
Chromium (Cr), % 16.5 to 18.5
15 to 17
Iron (Fe), % 62.3 to 70.5
41.7 to 51
Manganese (Mn), % 0 to 2.0
0 to 2.0
Molybdenum (Mo), % 2.5 to 3.0
0
Nickel (Ni), % 10.5 to 13
33 to 37
Nitrogen (N), % 0 to 0.1
0 to 0.1
Phosphorus (P), % 0 to 0.045
0 to 0.045
Silicon (Si), % 0 to 1.0
1.0 to 2.0
Sulfur (S), % 0 to 0.015
0 to 0.015