EN 1.4432 Stainless Steel vs. C92200 Bronze

EN 1.4432 stainless steel belongs to the iron alloys classification, while C92200 bronze belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is EN 1.4432 stainless steel and the bottom bar is C92200 bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
110
Elongation at Break, % 44
25
Fatigue Strength, MPa 220
76
Poisson's Ratio 0.28
0.34
Shear Modulus, GPa 78
41
Tensile Strength: Ultimate (UTS), MPa 610
280
Tensile Strength: Yield (Proof), MPa 250
140

Thermal Properties

Latent Heat of Fusion, J/g 290
190
Maximum Temperature: Mechanical, °C 960
170
Melting Completion (Liquidus), °C 1450
990
Melting Onset (Solidus), °C 1400
830
Specific Heat Capacity, J/kg-K 470
370
Thermal Conductivity, W/m-K 15
70
Thermal Expansion, µm/m-K 16
19

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.3
14
Electrical Conductivity: Equal Weight (Specific), % IACS 2.6
14

Otherwise Unclassified Properties

Base Metal Price, % relative 19
32
Density, g/cm3 7.9
8.7
Embodied Carbon, kg CO2/kg material 3.9
3.2
Embodied Energy, MJ/kg 54
52
Embodied Water, L/kg 150
360

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 220
58
Resilience: Unit (Modulus of Resilience), kJ/m3 150
87
Stiffness to Weight: Axial, points 14
6.9
Stiffness to Weight: Bending, points 25
18
Strength to Weight: Axial, points 21
8.9
Strength to Weight: Bending, points 20
11
Thermal Diffusivity, mm2/s 4.0
21
Thermal Shock Resistance, points 14
9.9

Alloy Composition

Aluminum (Al), % 0
0 to 0.0050
Antimony (Sb), % 0
0 to 0.25
Carbon (C), % 0 to 0.030
0
Chromium (Cr), % 16.5 to 18.5
0
Copper (Cu), % 0
86 to 90
Iron (Fe), % 62.3 to 70.5
0 to 0.25
Lead (Pb), % 0
1.0 to 2.0
Manganese (Mn), % 0 to 2.0
0
Molybdenum (Mo), % 2.5 to 3.0
0
Nickel (Ni), % 10.5 to 13
0 to 1.0
Nitrogen (N), % 0 to 0.1
0
Phosphorus (P), % 0 to 0.045
0 to 1.5
Silicon (Si), % 0 to 1.0
0 to 0.0050
Sulfur (S), % 0 to 0.015
0 to 0.050
Tin (Sn), % 0
5.5 to 6.5
Zinc (Zn), % 0
3.0 to 5.0
Residuals, % 0
0 to 0.7