EN 1.4435 Stainless Steel vs. N08120 Nickel

EN 1.4435 stainless steel belongs to the iron alloys classification, while N08120 nickel belongs to the nickel alloys. They have 66% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is EN 1.4435 stainless steel and the bottom bar is N08120 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 43
34
Fatigue Strength, MPa 220
230
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 78
79
Shear Strength, MPa 420
470
Tensile Strength: Ultimate (UTS), MPa 610
700
Tensile Strength: Yield (Proof), MPa 240
310

Thermal Properties

Latent Heat of Fusion, J/g 290
310
Maximum Temperature: Mechanical, °C 980
1000
Melting Completion (Liquidus), °C 1440
1420
Melting Onset (Solidus), °C 1400
1370
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 15
11
Thermal Expansion, µm/m-K 16
14

Otherwise Unclassified Properties

Base Metal Price, % relative 21
45
Density, g/cm3 7.9
8.2
Embodied Carbon, kg CO2/kg material 4.1
7.2
Embodied Energy, MJ/kg 57
100
Embodied Water, L/kg 160
240

Common Calculations

PREN (Pitting Resistance) 28
35
Resilience: Ultimate (Unit Rupture Work), MJ/m3 210
190
Resilience: Unit (Modulus of Resilience), kJ/m3 150
240
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 21
24
Strength to Weight: Bending, points 20
21
Thermal Diffusivity, mm2/s 4.0
3.0
Thermal Shock Resistance, points 14
17

Alloy Composition

Aluminum (Al), % 0
0 to 0.4
Boron (B), % 0
0 to 0.010
Carbon (C), % 0 to 0.030
0.020 to 0.1
Chromium (Cr), % 17 to 19
23 to 27
Cobalt (Co), % 0
0 to 3.0
Copper (Cu), % 0
0 to 0.5
Iron (Fe), % 59.8 to 68
21 to 41.4
Manganese (Mn), % 0 to 2.0
0 to 1.5
Molybdenum (Mo), % 2.5 to 3.0
0 to 2.5
Nickel (Ni), % 12.5 to 15
35 to 39
Niobium (Nb), % 0
0.4 to 0.9
Nitrogen (N), % 0 to 0.1
0.15 to 0.3
Phosphorus (P), % 0 to 0.045
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.015
0 to 0.030
Titanium (Ti), % 0
0 to 0.2
Tungsten (W), % 0
0 to 2.5