EN 1.4436 Stainless Steel vs. AISI 205 Stainless Steel

Both EN 1.4436 stainless steel and AISI 205 stainless steel are iron alloys. They have 86% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is EN 1.4436 stainless steel and the bottom bar is AISI 205 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
210 to 440
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 42
11 to 51
Fatigue Strength, MPa 220
410 to 640
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 78
77
Shear Strength, MPa 430
560 to 850
Tensile Strength: Ultimate (UTS), MPa 620
800 to 1430
Tensile Strength: Yield (Proof), MPa 240
450 to 1100

Thermal Properties

Latent Heat of Fusion, J/g 290
280
Maximum Temperature: Corrosion, °C 410
410
Maximum Temperature: Mechanical, °C 960
880
Melting Completion (Liquidus), °C 1450
1380
Melting Onset (Solidus), °C 1400
1340
Specific Heat Capacity, J/kg-K 470
480
Thermal Expansion, µm/m-K 16
18

Otherwise Unclassified Properties

Base Metal Price, % relative 19
11
Density, g/cm3 7.9
7.6
Embodied Carbon, kg CO2/kg material 3.9
2.6
Embodied Energy, MJ/kg 54
37
Embodied Water, L/kg 150
150

Common Calculations

PREN (Pitting Resistance) 27
23
Resilience: Ultimate (Unit Rupture Work), MJ/m3 210
150 to 430
Resilience: Unit (Modulus of Resilience), kJ/m3 150
510 to 3060
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
26
Strength to Weight: Axial, points 22
29 to 52
Strength to Weight: Bending, points 20
25 to 37
Thermal Shock Resistance, points 14
16 to 29

Alloy Composition

Carbon (C), % 0 to 0.050
0.12 to 0.25
Chromium (Cr), % 16.5 to 18.5
16.5 to 18.5
Iron (Fe), % 62.3 to 70.5
62.6 to 68.1
Manganese (Mn), % 0 to 2.0
14 to 15.5
Molybdenum (Mo), % 2.5 to 3.0
0
Nickel (Ni), % 10.5 to 13
1.0 to 1.7
Nitrogen (N), % 0 to 0.1
0.32 to 0.4
Phosphorus (P), % 0 to 0.045
0 to 0.060
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.015
0 to 0.030