EN 1.4438 Stainless Steel vs. EN 1.1233 Steel

Both EN 1.4438 stainless steel and EN 1.1233 steel are iron alloys. They have 63% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is EN 1.4438 stainless steel and the bottom bar is EN 1.1233 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
200 to 220
Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 79
72
Tensile Strength: Ultimate (UTS), MPa 620
680 to 760

Thermal Properties

Latent Heat of Fusion, J/g 290
250
Maximum Temperature: Mechanical, °C 1000
400
Melting Completion (Liquidus), °C 1450
1450
Melting Onset (Solidus), °C 1400
1410
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 14
51
Thermal Expansion, µm/m-K 16
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 2.3
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 22
1.9
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 4.4
1.4
Embodied Energy, MJ/kg 60
19
Embodied Water, L/kg 160
47

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 22
24 to 27
Strength to Weight: Bending, points 20
22 to 24
Thermal Diffusivity, mm2/s 3.7
14
Thermal Shock Resistance, points 14
22 to 24

Alloy Composition

Aluminum (Al), % 0
0 to 0.050
Carbon (C), % 0 to 0.030
0.52 to 0.6
Chromium (Cr), % 17.5 to 19.5
0
Copper (Cu), % 0
0 to 0.3
Iron (Fe), % 57.3 to 66.5
98 to 99.1
Manganese (Mn), % 0 to 2.0
0.9 to 1.2
Molybdenum (Mo), % 3.0 to 4.0
0
Nickel (Ni), % 13 to 16
0
Nitrogen (N), % 0 to 0.1
0
Oxygen (O), % 0
0 to 0.0020
Phosphorus (P), % 0 to 0.045
0 to 0.025
Silicon (Si), % 0 to 1.0
0 to 0.4
Sulfur (S), % 0 to 0.015
0 to 0.030