EN 1.4439 Stainless Steel vs. C34200 Brass

EN 1.4439 stainless steel belongs to the iron alloys classification, while C34200 brass belongs to the copper alloys. There are 29 material properties with values for both materials. Properties with values for just one material (7, in this case) are not shown.

For each property being compared, the top bar is EN 1.4439 stainless steel and the bottom bar is C34200 brass.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
100
Elongation at Break, % 40
3.0 to 17
Poisson's Ratio 0.28
0.31
Shear Modulus, GPa 79
40
Shear Strength, MPa 470
230 to 360
Tensile Strength: Ultimate (UTS), MPa 680
370 to 650
Tensile Strength: Yield (Proof), MPa 310
150 to 420

Thermal Properties

Latent Heat of Fusion, J/g 290
170
Maximum Temperature: Mechanical, °C 980
120
Melting Completion (Liquidus), °C 1460
910
Melting Onset (Solidus), °C 1410
890
Specific Heat Capacity, J/kg-K 470
380
Thermal Conductivity, W/m-K 14
120
Thermal Expansion, µm/m-K 16
21

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
26
Electrical Conductivity: Equal Weight (Specific), % IACS 2.3
29

Otherwise Unclassified Properties

Base Metal Price, % relative 22
24
Density, g/cm3 7.9
8.2
Embodied Carbon, kg CO2/kg material 4.5
2.6
Embodied Energy, MJ/kg 61
45
Embodied Water, L/kg 160
320

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 220
9.0 to 98
Resilience: Unit (Modulus of Resilience), kJ/m3 240
110 to 870
Stiffness to Weight: Axial, points 14
7.1
Stiffness to Weight: Bending, points 25
19
Strength to Weight: Axial, points 24
13 to 22
Strength to Weight: Bending, points 22
14 to 20
Thermal Diffusivity, mm2/s 3.8
37
Thermal Shock Resistance, points 15
12 to 22

Alloy Composition

Carbon (C), % 0 to 0.030
0
Chromium (Cr), % 16.5 to 18.5
0
Copper (Cu), % 0
62 to 65
Iron (Fe), % 58.7 to 66.9
0 to 0.1
Lead (Pb), % 0
1.5 to 2.5
Manganese (Mn), % 0 to 2.0
0
Molybdenum (Mo), % 4.0 to 5.0
0
Nickel (Ni), % 12.5 to 14.5
0
Nitrogen (N), % 0.12 to 0.22
0
Phosphorus (P), % 0 to 0.045
0
Silicon (Si), % 0 to 1.0
0
Sulfur (S), % 0 to 0.015
0
Zinc (Zn), % 0
32 to 36.5
Residuals, % 0
0 to 0.4