EN 1.4439 Stainless Steel vs. N06110 Nickel

EN 1.4439 stainless steel belongs to the iron alloys classification, while N06110 nickel belongs to the nickel alloys. They have a modest 37% of their average alloy composition in common, which, by itself, doesn't mean much. There are 26 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is EN 1.4439 stainless steel and the bottom bar is N06110 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
210
Elongation at Break, % 40
53
Fatigue Strength, MPa 270
320
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 79
84
Shear Strength, MPa 470
530
Tensile Strength: Ultimate (UTS), MPa 680
730
Tensile Strength: Yield (Proof), MPa 310
330

Thermal Properties

Latent Heat of Fusion, J/g 290
340
Maximum Temperature: Mechanical, °C 980
1020
Melting Completion (Liquidus), °C 1460
1490
Melting Onset (Solidus), °C 1410
1440
Specific Heat Capacity, J/kg-K 470
440
Thermal Expansion, µm/m-K 16
12

Otherwise Unclassified Properties

Base Metal Price, % relative 22
65
Density, g/cm3 7.9
8.6
Embodied Carbon, kg CO2/kg material 4.5
11
Embodied Energy, MJ/kg 61
160
Embodied Water, L/kg 160
320

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 220
320
Resilience: Unit (Modulus of Resilience), kJ/m3 240
260
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
23
Strength to Weight: Axial, points 24
23
Strength to Weight: Bending, points 22
21
Thermal Shock Resistance, points 15
20

Alloy Composition

Aluminum (Al), % 0
0 to 1.0
Carbon (C), % 0 to 0.030
0 to 0.15
Chromium (Cr), % 16.5 to 18.5
28 to 33
Copper (Cu), % 0
0 to 0.5
Iron (Fe), % 58.7 to 66.9
0 to 1.0
Manganese (Mn), % 0 to 2.0
0 to 1.0
Molybdenum (Mo), % 4.0 to 5.0
9.0 to 12
Nickel (Ni), % 12.5 to 14.5
51 to 62
Niobium (Nb), % 0
0 to 1.0
Nitrogen (N), % 0.12 to 0.22
0
Phosphorus (P), % 0 to 0.045
0 to 0.5
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.015
0 to 0.015
Titanium (Ti), % 0
0 to 1.0
Tungsten (W), % 0
1.0 to 4.0