EN 1.4446 Stainless Steel vs. EN 1.5402 Steel

Both EN 1.4446 stainless steel and EN 1.5402 steel are iron alloys. They have 65% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4446 stainless steel and the bottom bar is EN 1.5402 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 140
180
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 23
23
Fatigue Strength, MPa 160
260
Impact Strength: V-Notched Charpy, J 56
45
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 79
73
Tensile Strength: Ultimate (UTS), MPa 490
580
Tensile Strength: Yield (Proof), MPa 240
370

Thermal Properties

Latent Heat of Fusion, J/g 290
250
Maximum Temperature: Mechanical, °C 980
410
Melting Completion (Liquidus), °C 1460
1470
Melting Onset (Solidus), °C 1410
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 14
51
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 22
2.4
Density, g/cm3 7.9
7.9
Embodied Carbon, kg CO2/kg material 4.5
1.7
Embodied Energy, MJ/kg 60
22
Embodied Water, L/kg 160
49

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 93
120
Resilience: Unit (Modulus of Resilience), kJ/m3 140
360
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 17
21
Strength to Weight: Bending, points 17
20
Thermal Diffusivity, mm2/s 3.6
14
Thermal Shock Resistance, points 11
17

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.18
Chromium (Cr), % 16.5 to 18.5
0
Iron (Fe), % 59.7 to 66.9
97.3 to 98.7
Manganese (Mn), % 0 to 1.5
0.9 to 1.4
Molybdenum (Mo), % 4.0 to 4.5
0.4 to 0.6
Nickel (Ni), % 12.5 to 14.5
0
Nitrogen (N), % 0.12 to 0.22
0
Phosphorus (P), % 0 to 0.040
0 to 0.025
Silicon (Si), % 0 to 1.0
0 to 0.4
Sulfur (S), % 0 to 0.030
0 to 0.015
Vanadium (V), % 0
0.040 to 0.080