EN 1.4449 Stainless Steel vs. ASTM A266 Carbon Steel

Both EN 1.4449 stainless steel and ASTM A266 carbon steel are iron alloys. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.4449 stainless steel and the bottom bar is ASTM A266 carbon steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 190
150 to 180
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 48
21 to 26
Fatigue Strength, MPa 240
170 to 200
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 78
73
Shear Strength, MPa 440
320 to 380
Tensile Strength: Ultimate (UTS), MPa 620
500 to 600
Tensile Strength: Yield (Proof), MPa 250
230 to 290

Thermal Properties

Latent Heat of Fusion, J/g 290
250
Maximum Temperature: Mechanical, °C 960
400
Melting Completion (Liquidus), °C 1440
1460
Melting Onset (Solidus), °C 1400
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 15
51 to 52
Thermal Expansion, µm/m-K 16
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.3
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 2.6
8.1 to 8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 19
1.8
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 3.9
1.4
Embodied Energy, MJ/kg 54
18 to 19
Embodied Water, L/kg 150
46 to 47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 240
110
Resilience: Unit (Modulus of Resilience), kJ/m3 160
140 to 230
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 22
18 to 21
Strength to Weight: Bending, points 20
18 to 20
Thermal Diffusivity, mm2/s 4.0
14
Thermal Shock Resistance, points 14
16 to 19