EN 1.4466 Stainless Steel vs. EN 1.4922 Stainless Steel

Both EN 1.4466 stainless steel and EN 1.4922 stainless steel are iron alloys. They have 63% of their average alloy composition in common. There are 33 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is EN 1.4466 stainless steel and the bottom bar is EN 1.4922 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 42
16
Fatigue Strength, MPa 250
330
Impact Strength: V-Notched Charpy, J 90
38
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 80
76
Shear Strength, MPa 440
470
Tensile Strength: Ultimate (UTS), MPa 640
770
Tensile Strength: Yield (Proof), MPa 280
550

Thermal Properties

Latent Heat of Fusion, J/g 300
270
Maximum Temperature: Corrosion, °C 450
380
Maximum Temperature: Mechanical, °C 1100
720
Melting Completion (Liquidus), °C 1420
1460
Melting Onset (Solidus), °C 1380
1410
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 14
24
Thermal Expansion, µm/m-K 16
11

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
2.9
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
3.3

Otherwise Unclassified Properties

Base Metal Price, % relative 28
7.5
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 5.0
2.8
Embodied Energy, MJ/kg 70
40
Embodied Water, L/kg 200
100

Common Calculations

PREN (Pitting Resistance) 35
15
Resilience: Ultimate (Unit Rupture Work), MJ/m3 220
110
Resilience: Unit (Modulus of Resilience), kJ/m3 200
770
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 22
27
Strength to Weight: Bending, points 21
24
Thermal Diffusivity, mm2/s 3.7
6.5
Thermal Shock Resistance, points 14
27

Alloy Composition

Carbon (C), % 0 to 0.020
0.17 to 0.23
Chromium (Cr), % 24 to 26
10 to 12.5
Iron (Fe), % 45.6 to 52.9
83.5 to 88.2
Manganese (Mn), % 0 to 2.0
0.3 to 1.0
Molybdenum (Mo), % 2.0 to 2.5
0.8 to 1.2
Nickel (Ni), % 21 to 23
0.3 to 0.8
Nitrogen (N), % 0.1 to 0.16
0
Phosphorus (P), % 0 to 0.025
0 to 0.025
Silicon (Si), % 0 to 0.7
0 to 0.4
Sulfur (S), % 0 to 0.010
0 to 0.015
Vanadium (V), % 0
0.2 to 0.35