EN 1.4468 Stainless Steel vs. CC331G Bronze

EN 1.4468 stainless steel belongs to the iron alloys classification, while CC331G bronze belongs to the copper alloys. There are 28 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is EN 1.4468 stainless steel and the bottom bar is CC331G bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
110
Elongation at Break, % 25
20
Poisson's Ratio 0.27
0.34
Shear Modulus, GPa 80
43
Tensile Strength: Ultimate (UTS), MPa 730
620
Tensile Strength: Yield (Proof), MPa 550
240

Thermal Properties

Latent Heat of Fusion, J/g 300
230
Maximum Temperature: Mechanical, °C 1100
220
Melting Completion (Liquidus), °C 1440
1060
Melting Onset (Solidus), °C 1400
1000
Specific Heat Capacity, J/kg-K 480
440
Thermal Conductivity, W/m-K 17
61
Thermal Expansion, µm/m-K 13
18

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
13
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
14

Otherwise Unclassified Properties

Base Metal Price, % relative 19
28
Density, g/cm3 7.8
8.3
Embodied Carbon, kg CO2/kg material 3.8
3.2
Embodied Energy, MJ/kg 53
53
Embodied Water, L/kg 180
390

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 170
97
Resilience: Unit (Modulus of Resilience), kJ/m3 730
250
Stiffness to Weight: Axial, points 15
7.6
Stiffness to Weight: Bending, points 25
19
Strength to Weight: Axial, points 26
21
Strength to Weight: Bending, points 23
19
Thermal Diffusivity, mm2/s 4.6
17
Thermal Shock Resistance, points 20
22

Alloy Composition

Aluminum (Al), % 0
8.5 to 10.5
Carbon (C), % 0 to 0.030
0
Chromium (Cr), % 24.5 to 26.5
0
Copper (Cu), % 0
83 to 86.5
Iron (Fe), % 59.7 to 67.4
1.5 to 3.5
Lead (Pb), % 0
0 to 0.1
Magnesium (Mg), % 0
0 to 0.050
Manganese (Mn), % 0 to 2.0
0 to 1.0
Molybdenum (Mo), % 2.5 to 3.5
0
Nickel (Ni), % 5.5 to 7.0
0 to 1.5
Nitrogen (N), % 0.12 to 0.25
0
Phosphorus (P), % 0 to 0.035
0
Silicon (Si), % 0 to 1.0
0 to 0.2
Sulfur (S), % 0 to 0.025
0
Tin (Sn), % 0
0 to 0.2
Zinc (Zn), % 0
0 to 0.5