EN 1.4468 Stainless Steel vs. SAE-AISI 1330 Steel

Both EN 1.4468 stainless steel and SAE-AISI 1330 steel are iron alloys. They have 65% of their average alloy composition in common. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is EN 1.4468 stainless steel and the bottom bar is SAE-AISI 1330 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 25
11 to 23
Fatigue Strength, MPa 380
210 to 380
Poisson's Ratio 0.27
0.29
Shear Modulus, GPa 80
73
Tensile Strength: Ultimate (UTS), MPa 730
520 to 710
Tensile Strength: Yield (Proof), MPa 550
290 to 610

Thermal Properties

Latent Heat of Fusion, J/g 300
250
Maximum Temperature: Mechanical, °C 1100
400
Melting Completion (Liquidus), °C 1440
1460
Melting Onset (Solidus), °C 1400
1410
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 17
51
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
7.2
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
8.3

Otherwise Unclassified Properties

Base Metal Price, % relative 19
1.9
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 3.8
1.4
Embodied Energy, MJ/kg 53
19
Embodied Water, L/kg 180
48

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 170
76 to 100
Resilience: Unit (Modulus of Resilience), kJ/m3 730
230 to 990
Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 26
19 to 25
Strength to Weight: Bending, points 23
18 to 23
Thermal Diffusivity, mm2/s 4.6
14
Thermal Shock Resistance, points 20
17 to 23

Alloy Composition

Carbon (C), % 0 to 0.030
0.28 to 0.33
Chromium (Cr), % 24.5 to 26.5
0
Iron (Fe), % 59.7 to 67.4
97.3 to 98
Manganese (Mn), % 0 to 2.0
1.6 to 1.9
Molybdenum (Mo), % 2.5 to 3.5
0
Nickel (Ni), % 5.5 to 7.0
0
Nitrogen (N), % 0.12 to 0.25
0
Phosphorus (P), % 0 to 0.035
0 to 0.035
Silicon (Si), % 0 to 1.0
0.15 to 0.35
Sulfur (S), % 0 to 0.025
0 to 0.040