EN 1.4469 Stainless Steel vs. ASTM A225 Steel

Both EN 1.4469 stainless steel and ASTM A225 steel are iron alloys. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown.

For each property being compared, the top bar is EN 1.4469 stainless steel and the bottom bar is ASTM A225 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
190
Elongation at Break, % 25
21 to 23
Fatigue Strength, MPa 380
330 to 390
Poisson's Ratio 0.27
0.29
Shear Modulus, GPa 81
73
Tensile Strength: Ultimate (UTS), MPa 740
620 to 830
Tensile Strength: Yield (Proof), MPa 550
460 to 550

Thermal Properties

Latent Heat of Fusion, J/g 300
250
Maximum Temperature: Mechanical, °C 1100
400
Melting Completion (Liquidus), °C 1450
1460
Melting Onset (Solidus), °C 1400
1420
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 17
52
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
7.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
8.4

Otherwise Unclassified Properties

Base Metal Price, % relative 21
2.3
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 4.1
1.8
Embodied Energy, MJ/kg 57
24 to 25
Embodied Water, L/kg 180
48

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 170
120 to 170
Resilience: Unit (Modulus of Resilience), kJ/m3 730
580 to 820
Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 26
22 to 29
Strength to Weight: Bending, points 23
21 to 25
Thermal Diffusivity, mm2/s 4.6
14
Thermal Shock Resistance, points 20
18 to 24