EN 1.4469 Stainless Steel vs. S30530 Stainless Steel

Both EN 1.4469 stainless steel and S30530 stainless steel are iron alloys. They have 90% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.4469 stainless steel and the bottom bar is S30530 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
200
Elongation at Break, % 25
46
Fatigue Strength, MPa 380
210
Poisson's Ratio 0.27
0.28
Shear Modulus, GPa 81
77
Tensile Strength: Ultimate (UTS), MPa 740
590
Tensile Strength: Yield (Proof), MPa 550
230

Thermal Properties

Latent Heat of Fusion, J/g 300
310
Maximum Temperature: Corrosion, °C 450
420
Maximum Temperature: Mechanical, °C 1100
970
Melting Completion (Liquidus), °C 1450
1410
Melting Onset (Solidus), °C 1400
1370
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 17
15
Thermal Expansion, µm/m-K 13
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 21
18
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 4.1
3.4
Embodied Energy, MJ/kg 57
48
Embodied Water, L/kg 180
150

Common Calculations

PREN (Pitting Resistance) 42
22
Resilience: Ultimate (Unit Rupture Work), MJ/m3 170
210
Resilience: Unit (Modulus of Resilience), kJ/m3 730
130
Stiffness to Weight: Axial, points 15
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 26
21
Strength to Weight: Bending, points 23
20
Thermal Diffusivity, mm2/s 4.6
4.1
Thermal Shock Resistance, points 20
13

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.080
Chromium (Cr), % 25 to 27
17 to 20.5
Copper (Cu), % 0 to 1.3
0.75 to 3.5
Iron (Fe), % 56.4 to 65.9
58.4 to 72.5
Manganese (Mn), % 0 to 1.0
0 to 2.0
Molybdenum (Mo), % 3.0 to 5.0
0.75 to 1.5
Nickel (Ni), % 6.0 to 8.0
8.5 to 11.5
Nitrogen (N), % 0.12 to 0.22
0
Phosphorus (P), % 0 to 0.035
0 to 0.045
Silicon (Si), % 0 to 1.0
0.5 to 2.5
Sulfur (S), % 0 to 0.025
0 to 0.030