EN 1.4477 Stainless Steel vs. N10629 Nickel

EN 1.4477 stainless steel belongs to the iron alloys classification, while N10629 nickel belongs to the nickel alloys. There are 26 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is EN 1.4477 stainless steel and the bottom bar is N10629 nickel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
220
Elongation at Break, % 22 to 23
45
Fatigue Strength, MPa 420 to 490
340
Poisson's Ratio 0.27
0.31
Shear Modulus, GPa 81
83
Shear Strength, MPa 550 to 580
600
Tensile Strength: Ultimate (UTS), MPa 880 to 930
860
Tensile Strength: Yield (Proof), MPa 620 to 730
400

Thermal Properties

Latent Heat of Fusion, J/g 300
310
Maximum Temperature: Mechanical, °C 1100
910
Melting Completion (Liquidus), °C 1430
1610
Melting Onset (Solidus), °C 1380
1560
Specific Heat Capacity, J/kg-K 480
390
Thermal Expansion, µm/m-K 13
10

Otherwise Unclassified Properties

Base Metal Price, % relative 20
75
Density, g/cm3 7.7
9.2
Embodied Carbon, kg CO2/kg material 3.7
15
Embodied Energy, MJ/kg 52
190
Embodied Water, L/kg 190
270

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 180 to 190
320
Resilience: Unit (Modulus of Resilience), kJ/m3 940 to 1290
360
Stiffness to Weight: Axial, points 15
13
Stiffness to Weight: Bending, points 25
22
Strength to Weight: Axial, points 31 to 33
26
Strength to Weight: Bending, points 26 to 27
22
Thermal Shock Resistance, points 23 to 25
27

Alloy Composition

Aluminum (Al), % 0
0.1 to 0.5
Carbon (C), % 0 to 0.030
0 to 0.010
Chromium (Cr), % 28 to 30
0.5 to 1.5
Cobalt (Co), % 0
0 to 2.5
Copper (Cu), % 0 to 0.8
0 to 0.5
Iron (Fe), % 56.6 to 63.6
1.0 to 6.0
Manganese (Mn), % 0.8 to 1.5
0 to 1.5
Molybdenum (Mo), % 1.5 to 2.6
26 to 30
Nickel (Ni), % 5.8 to 7.5
65 to 72.4
Nitrogen (N), % 0.3 to 0.4
0
Phosphorus (P), % 0 to 0.030
0 to 0.040
Silicon (Si), % 0 to 0.5
0 to 0.050
Sulfur (S), % 0 to 0.015
0 to 0.010