EN 1.4482 Stainless Steel vs. AISI 430F Stainless Steel

Both EN 1.4482 stainless steel and AISI 430F stainless steel are iron alloys. They have 89% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4482 stainless steel and the bottom bar is AISI 430F stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 34
23
Fatigue Strength, MPa 420 to 450
210
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 78
77
Shear Strength, MPa 510 to 530
340
Tensile Strength: Ultimate (UTS), MPa 770 to 800
540
Tensile Strength: Yield (Proof), MPa 530 to 570
310

Thermal Properties

Latent Heat of Fusion, J/g 290
280
Maximum Temperature: Corrosion, °C 430
410
Maximum Temperature: Mechanical, °C 980
870
Melting Completion (Liquidus), °C 1420
1430
Melting Onset (Solidus), °C 1370
1390
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 15
25
Thermal Expansion, µm/m-K 13
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
2.8
Electrical Conductivity: Equal Weight (Specific), % IACS 2.6
3.3

Otherwise Unclassified Properties

Base Metal Price, % relative 12
8.5
Density, g/cm3 7.7
7.7
Embodied Carbon, kg CO2/kg material 2.7
2.1
Embodied Energy, MJ/kg 38
29
Embodied Water, L/kg 150
120

Common Calculations

PREN (Pitting Resistance) 24
17
Resilience: Ultimate (Unit Rupture Work), MJ/m3 230 to 250
110
Resilience: Unit (Modulus of Resilience), kJ/m3 690 to 820
250
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 28 to 29
20
Strength to Weight: Bending, points 24 to 25
19
Thermal Diffusivity, mm2/s 4.0
6.7
Thermal Shock Resistance, points 21 to 22
19

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.12
Chromium (Cr), % 19.5 to 21.5
16 to 18
Copper (Cu), % 0 to 1.0
0
Iron (Fe), % 66.1 to 74.9
79.2 to 83.9
Manganese (Mn), % 4.0 to 6.0
0 to 1.3
Molybdenum (Mo), % 0.1 to 0.6
0
Nickel (Ni), % 1.5 to 3.5
0
Nitrogen (N), % 0.050 to 0.2
0
Phosphorus (P), % 0 to 0.035
0 to 0.060
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.030
0.15 to 0.35