EN 1.4482 Stainless Steel vs. EN 1.4347 Stainless Steel

Both EN 1.4482 stainless steel and EN 1.4347 stainless steel are iron alloys. They have a moderately high 90% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4482 stainless steel and the bottom bar is EN 1.4347 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 34
23
Fatigue Strength, MPa 420 to 450
320
Poisson's Ratio 0.28
0.27
Shear Modulus, GPa 78
79
Tensile Strength: Ultimate (UTS), MPa 770 to 800
660
Tensile Strength: Yield (Proof), MPa 530 to 570
480

Thermal Properties

Latent Heat of Fusion, J/g 290
300
Maximum Temperature: Corrosion, °C 430
450
Maximum Temperature: Mechanical, °C 980
1100
Melting Completion (Liquidus), °C 1420
1410
Melting Onset (Solidus), °C 1370
1370
Specific Heat Capacity, J/kg-K 480
490
Thermal Conductivity, W/m-K 15
15
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 2.6
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 12
16
Density, g/cm3 7.7
7.7
Embodied Carbon, kg CO2/kg material 2.7
3.1
Embodied Energy, MJ/kg 38
44
Embodied Water, L/kg 150
170

Common Calculations

PREN (Pitting Resistance) 24
28
Resilience: Ultimate (Unit Rupture Work), MJ/m3 230 to 250
140
Resilience: Unit (Modulus of Resilience), kJ/m3 690 to 820
570
Stiffness to Weight: Axial, points 14
15
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 28 to 29
24
Strength to Weight: Bending, points 24 to 25
22
Thermal Diffusivity, mm2/s 4.0
4.0
Thermal Shock Resistance, points 21 to 22
19

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.050
Chromium (Cr), % 19.5 to 21.5
25 to 27
Copper (Cu), % 0 to 1.0
0
Iron (Fe), % 66.1 to 74.9
62.2 to 69.4
Manganese (Mn), % 4.0 to 6.0
0 to 1.5
Molybdenum (Mo), % 0.1 to 0.6
0
Nickel (Ni), % 1.5 to 3.5
5.5 to 7.5
Nitrogen (N), % 0.050 to 0.2
0.1 to 0.2
Phosphorus (P), % 0 to 0.035
0 to 0.035
Silicon (Si), % 0 to 1.0
0 to 1.5
Sulfur (S), % 0 to 0.030
0 to 0.020