EN 1.4482 Stainless Steel vs. Grade FDSiCr Steel
Both EN 1.4482 stainless steel and grade FDSiCr steel are iron alloys. They have 72% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.
For each property being compared, the top bar is EN 1.4482 stainless steel and the bottom bar is grade FDSiCr steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 190 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 78 | |
| 80 |
| Tensile Strength: Ultimate (UTS), MPa | 770 to 800 | |
| 1930 |
Thermal Properties
| Latent Heat of Fusion, J/g | 290 | |
| 270 |
| Maximum Temperature: Mechanical, °C | 980 | |
| 410 |
| Melting Completion (Liquidus), °C | 1420 | |
| 1440 |
| Melting Onset (Solidus), °C | 1370 | |
| 1400 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 480 |
| Thermal Conductivity, W/m-K | 15 | |
| 48 |
| Thermal Expansion, µm/m-K | 13 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.2 | |
| 7.3 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.6 | |
| 8.5 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 12 | |
| 2.2 |
| Density, g/cm3 | 7.7 | |
| 7.7 |
| Embodied Carbon, kg CO2/kg material | 2.7 | |
| 1.5 |
| Embodied Energy, MJ/kg | 38 | |
| 20 |
| Embodied Water, L/kg | 150 | |
| 48 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 25 |
| Strength to Weight: Axial, points | 28 to 29 | |
| 69 |
| Strength to Weight: Bending, points | 24 to 25 | |
| 44 |
| Thermal Diffusivity, mm2/s | 4.0 | |
| 13 |
| Thermal Shock Resistance, points | 21 to 22 | |
| 58 |
Alloy Composition
| Carbon (C), % | 0 to 0.030 | |
| 0.5 to 0.6 |
| Chromium (Cr), % | 19.5 to 21.5 | |
| 0.5 to 0.8 |
| Copper (Cu), % | 0 to 1.0 | |
| 0 to 0.12 |
| Iron (Fe), % | 66.1 to 74.9 | |
| 96.5 to 97.8 |
| Manganese (Mn), % | 4.0 to 6.0 | |
| 0.5 to 0.9 |
| Molybdenum (Mo), % | 0.1 to 0.6 | |
| 0 |
| Nickel (Ni), % | 1.5 to 3.5 | |
| 0 |
| Nitrogen (N), % | 0.050 to 0.2 | |
| 0 |
| Phosphorus (P), % | 0 to 0.035 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 to 1.0 | |
| 1.2 to 1.6 |
| Sulfur (S), % | 0 to 0.030 | |
| 0 to 0.025 |