EN 1.4482 Stainless Steel vs. Grade VDC Steel

Both EN 1.4482 stainless steel and grade VDC steel are iron alloys. They have 72% of their average alloy composition in common. There are 24 material properties with values for both materials. Properties with values for just one material (10, in this case) are not shown.

For each property being compared, the top bar is EN 1.4482 stainless steel and the bottom bar is grade VDC steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
190
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 78
80
Tensile Strength: Ultimate (UTS), MPa 770 to 800
1700

Thermal Properties

Latent Heat of Fusion, J/g 290
250
Maximum Temperature: Mechanical, °C 980
400
Melting Completion (Liquidus), °C 1420
1450
Melting Onset (Solidus), °C 1370
1410
Specific Heat Capacity, J/kg-K 480
470
Thermal Conductivity, W/m-K 15
51
Thermal Expansion, µm/m-K 13
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 2.6
8.1

Otherwise Unclassified Properties

Base Metal Price, % relative 12
1.9
Density, g/cm3 7.7
7.8
Embodied Carbon, kg CO2/kg material 2.7
1.4
Embodied Energy, MJ/kg 38
19
Embodied Water, L/kg 150
47

Common Calculations

Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 28 to 29
60
Strength to Weight: Bending, points 24 to 25
40
Thermal Diffusivity, mm2/s 4.0
14
Thermal Shock Resistance, points 21 to 22
50

Alloy Composition

Carbon (C), % 0 to 0.030
0.6 to 0.75
Chromium (Cr), % 19.5 to 21.5
0 to 0.3
Copper (Cu), % 0 to 1.0
0 to 0.060
Iron (Fe), % 66.1 to 74.9
98.3 to 99.35
Manganese (Mn), % 4.0 to 6.0
0.5 to 1.0
Molybdenum (Mo), % 0.1 to 0.6
0
Nickel (Ni), % 1.5 to 3.5
0
Nitrogen (N), % 0.050 to 0.2
0
Phosphorus (P), % 0 to 0.035
0 to 0.020
Silicon (Si), % 0 to 1.0
0.15 to 0.3
Sulfur (S), % 0 to 0.030
0 to 0.020