EN 1.4507 Stainless Steel vs. EN 1.0402 Steel

Both EN 1.4507 stainless steel and EN 1.0402 steel are iron alloys. They have 62% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4507 stainless steel and the bottom bar is EN 1.0402 steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 230
130
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 25
24
Fatigue Strength, MPa 410
170
Poisson's Ratio 0.27
0.29
Shear Modulus, GPa 80
73
Shear Strength, MPa 530
290
Tensile Strength: Ultimate (UTS), MPa 840
460
Tensile Strength: Yield (Proof), MPa 590
240

Thermal Properties

Latent Heat of Fusion, J/g 300
250
Maximum Temperature: Mechanical, °C 1100
400
Melting Completion (Liquidus), °C 1440
1460
Melting Onset (Solidus), °C 1390
1420
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 15
50
Thermal Expansion, µm/m-K 13
12

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
7.1
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
8.2

Otherwise Unclassified Properties

Base Metal Price, % relative 21
2.1
Density, g/cm3 7.8
7.8
Embodied Carbon, kg CO2/kg material 4.0
1.4
Embodied Energy, MJ/kg 55
19
Embodied Water, L/kg 180
47

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 190
94
Resilience: Unit (Modulus of Resilience), kJ/m3 850
150
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 30
16
Strength to Weight: Bending, points 25
17
Thermal Diffusivity, mm2/s 4.0
13
Thermal Shock Resistance, points 23
15

Alloy Composition

Carbon (C), % 0 to 0.030
0.17 to 0.24
Chromium (Cr), % 24 to 26
0 to 0.4
Copper (Cu), % 1.0 to 2.5
0
Iron (Fe), % 56.4 to 65.8
97.7 to 99.43
Manganese (Mn), % 0 to 2.0
0.4 to 0.7
Molybdenum (Mo), % 3.0 to 4.0
0 to 0.1
Nickel (Ni), % 6.0 to 8.0
0 to 0.4
Nitrogen (N), % 0.2 to 0.3
0
Phosphorus (P), % 0 to 0.035
0 to 0.045
Silicon (Si), % 0 to 0.7
0 to 0.4
Sulfur (S), % 0 to 0.015
0 to 0.045