EN 1.4511 Stainless Steel vs. 711.0 Aluminum

EN 1.4511 stainless steel belongs to the iron alloys classification, while 711.0 aluminum belongs to the aluminum alloys. There are 30 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN 1.4511 stainless steel and the bottom bar is 711.0 aluminum.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 180
70
Elastic (Young's, Tensile) Modulus, GPa 200
71
Elongation at Break, % 25
7.8
Fatigue Strength, MPa 180
100
Poisson's Ratio 0.28
0.32
Shear Modulus, GPa 77
27
Tensile Strength: Ultimate (UTS), MPa 510
220
Tensile Strength: Yield (Proof), MPa 260
140

Thermal Properties

Latent Heat of Fusion, J/g 280
380
Maximum Temperature: Mechanical, °C 870
170
Melting Completion (Liquidus), °C 1440
640
Melting Onset (Solidus), °C 1400
610
Specific Heat Capacity, J/kg-K 480
860
Thermal Conductivity, W/m-K 25
160
Thermal Expansion, µm/m-K 10
24

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
40
Electrical Conductivity: Equal Weight (Specific), % IACS 3.3
120

Otherwise Unclassified Properties

Base Metal Price, % relative 11
9.5
Density, g/cm3 7.7
3.0
Embodied Carbon, kg CO2/kg material 2.5
7.9
Embodied Energy, MJ/kg 37
150
Embodied Water, L/kg 120
1120

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
15
Resilience: Unit (Modulus of Resilience), kJ/m3 170
140
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
45
Strength to Weight: Axial, points 18
20
Strength to Weight: Bending, points 18
26
Thermal Diffusivity, mm2/s 6.7
61
Thermal Shock Resistance, points 19
9.3

Alloy Composition

Aluminum (Al), % 0
89.8 to 92.7
Carbon (C), % 0 to 0.050
0
Chromium (Cr), % 16 to 18
0
Copper (Cu), % 0
0.35 to 0.65
Iron (Fe), % 78.9 to 84
0.7 to 1.4
Magnesium (Mg), % 0
0.25 to 0.45
Manganese (Mn), % 0 to 1.0
0 to 0.050
Niobium (Nb), % 0 to 1.0
0
Phosphorus (P), % 0 to 0.040
0
Silicon (Si), % 0 to 1.0
0 to 0.3
Sulfur (S), % 0 to 0.015
0
Titanium (Ti), % 0
0 to 0.2
Zinc (Zn), % 0
6.0 to 7.0
Residuals, % 0
0 to 0.15