EN 1.4512 Stainless Steel vs. AWS ERTi-5

EN 1.4512 stainless steel belongs to the iron alloys classification, while AWS ERTi-5 belongs to the titanium alloys. There are 29 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4512 stainless steel and the bottom bar is AWS ERTi-5.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 190
110
Elongation at Break, % 28
10
Fatigue Strength, MPa 180
470
Poisson's Ratio 0.28
0.32
Shear Modulus, GPa 76
40
Tensile Strength: Ultimate (UTS), MPa 470
900
Tensile Strength: Yield (Proof), MPa 240
830

Thermal Properties

Latent Heat of Fusion, J/g 270
410
Maximum Temperature: Mechanical, °C 720
340
Melting Completion (Liquidus), °C 1450
1610
Melting Onset (Solidus), °C 1400
1560
Specific Heat Capacity, J/kg-K 480
560
Thermal Conductivity, W/m-K 25
7.1
Thermal Expansion, µm/m-K 11
9.6

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.9
1.0
Electrical Conductivity: Equal Weight (Specific), % IACS 3.3
2.0

Otherwise Unclassified Properties

Base Metal Price, % relative 6.5
36
Density, g/cm3 7.7
4.4
Embodied Carbon, kg CO2/kg material 2.0
38
Embodied Energy, MJ/kg 27
610
Embodied Water, L/kg 95
200

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 110
87
Resilience: Unit (Modulus of Resilience), kJ/m3 150
3250
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
35
Strength to Weight: Axial, points 17
56
Strength to Weight: Bending, points 17
46
Thermal Diffusivity, mm2/s 6.7
2.9
Thermal Shock Resistance, points 17
63

Alloy Composition

Aluminum (Al), % 0
5.5 to 6.8
Carbon (C), % 0 to 0.030
0 to 0.050
Chromium (Cr), % 10.5 to 12.5
0
Hydrogen (H), % 0
0 to 0.015
Iron (Fe), % 84.8 to 89.5
0 to 0.22
Manganese (Mn), % 0 to 1.0
0
Nitrogen (N), % 0
0 to 0.030
Oxygen (O), % 0
0.12 to 0.2
Phosphorus (P), % 0 to 0.040
0
Silicon (Si), % 0 to 1.0
0
Sulfur (S), % 0 to 0.015
0
Titanium (Ti), % 0 to 0.65
88.2 to 90.9
Vanadium (V), % 0
3.5 to 4.5