EN 1.4513 Stainless Steel vs. EN 1.4951 Stainless Steel

Both EN 1.4513 stainless steel and EN 1.4951 stainless steel are iron alloys. They have 71% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4513 stainless steel and the bottom bar is EN 1.4951 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 26
38
Fatigue Strength, MPa 170
190
Poisson's Ratio 0.28
0.27
Shear Modulus, GPa 77
79
Shear Strength, MPa 310
430
Tensile Strength: Ultimate (UTS), MPa 480
630
Tensile Strength: Yield (Proof), MPa 240
220

Thermal Properties

Latent Heat of Fusion, J/g 280
300
Maximum Temperature: Corrosion, °C 500
450
Maximum Temperature: Mechanical, °C 880
1100
Melting Completion (Liquidus), °C 1450
1410
Melting Onset (Solidus), °C 1410
1360
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 25
15
Thermal Expansion, µm/m-K 10
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.5
2.1
Electrical Conductivity: Equal Weight (Specific), % IACS 2.9
2.4

Otherwise Unclassified Properties

Base Metal Price, % relative 10
25
Density, g/cm3 7.7
7.9
Embodied Carbon, kg CO2/kg material 2.5
4.3
Embodied Energy, MJ/kg 35
61
Embodied Water, L/kg 120
190

Common Calculations

PREN (Pitting Resistance) 21
26
Resilience: Ultimate (Unit Rupture Work), MJ/m3 100
190
Resilience: Unit (Modulus of Resilience), kJ/m3 150
130
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 17
22
Strength to Weight: Bending, points 18
21
Thermal Diffusivity, mm2/s 6.8
3.9
Thermal Shock Resistance, points 17
14

Alloy Composition

Carbon (C), % 0 to 0.025
0.040 to 0.080
Chromium (Cr), % 16 to 18
24 to 26
Iron (Fe), % 77.7 to 83.1
49.1 to 57
Manganese (Mn), % 0 to 1.0
0 to 2.0
Molybdenum (Mo), % 0.8 to 1.4
0
Nickel (Ni), % 0
19 to 22
Nitrogen (N), % 0 to 0.020
0 to 0.1
Phosphorus (P), % 0 to 0.040
0 to 0.035
Silicon (Si), % 0 to 1.0
0 to 0.7
Sulfur (S), % 0 to 0.015
0 to 0.015
Titanium (Ti), % 0.15 to 0.8
0