EN 1.4513 Stainless Steel vs. Nickel 30

EN 1.4513 stainless steel belongs to the iron alloys classification, while nickel 30 belongs to the nickel alloys. They have a modest 34% of their average alloy composition in common, which, by itself, doesn't mean much. There are 30 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4513 stainless steel and the bottom bar is nickel 30.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
210
Elongation at Break, % 26
34
Fatigue Strength, MPa 170
200
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 77
82
Shear Strength, MPa 310
440
Tensile Strength: Ultimate (UTS), MPa 480
660
Tensile Strength: Yield (Proof), MPa 240
270

Thermal Properties

Latent Heat of Fusion, J/g 280
320
Maximum Temperature: Mechanical, °C 880
1020
Melting Completion (Liquidus), °C 1450
1480
Melting Onset (Solidus), °C 1410
1430
Specific Heat Capacity, J/kg-K 480
450
Thermal Conductivity, W/m-K 25
10
Thermal Expansion, µm/m-K 10
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.5
1.5
Electrical Conductivity: Equal Weight (Specific), % IACS 2.9
1.6

Otherwise Unclassified Properties

Base Metal Price, % relative 10
60
Density, g/cm3 7.7
8.5
Embodied Carbon, kg CO2/kg material 2.5
9.4
Embodied Energy, MJ/kg 35
130
Embodied Water, L/kg 120
290

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 100
180
Resilience: Unit (Modulus of Resilience), kJ/m3 150
180
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
23
Strength to Weight: Axial, points 17
22
Strength to Weight: Bending, points 18
20
Thermal Diffusivity, mm2/s 6.8
2.7
Thermal Shock Resistance, points 17
18

Alloy Composition

Carbon (C), % 0 to 0.025
0 to 0.030
Chromium (Cr), % 16 to 18
28 to 31.5
Cobalt (Co), % 0
0 to 5.0
Copper (Cu), % 0
1.0 to 2.4
Iron (Fe), % 77.7 to 83.1
13 to 17
Manganese (Mn), % 0 to 1.0
0 to 0.030
Molybdenum (Mo), % 0.8 to 1.4
4.0 to 6.0
Nickel (Ni), % 0
30.2 to 52.2
Niobium (Nb), % 0
0.3 to 1.5
Nitrogen (N), % 0 to 0.020
0
Phosphorus (P), % 0 to 0.040
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 0.8
Sulfur (S), % 0 to 0.015
0 to 0.020
Titanium (Ti), % 0.15 to 0.8
0
Tungsten (W), % 0
1.5 to 4.0