EN 1.4515 Stainless Steel vs. S42010 Stainless Steel

Both EN 1.4515 stainless steel and S42010 stainless steel are iron alloys. They have 79% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4515 stainless steel and the bottom bar is S42010 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 25
18
Fatigue Strength, MPa 380
220
Poisson's Ratio 0.27
0.28
Shear Modulus, GPa 80
76
Tensile Strength: Ultimate (UTS), MPa 730
590
Tensile Strength: Yield (Proof), MPa 550
350

Thermal Properties

Latent Heat of Fusion, J/g 300
280
Maximum Temperature: Corrosion, °C 450
390
Maximum Temperature: Mechanical, °C 1100
800
Melting Completion (Liquidus), °C 1440
1440
Melting Onset (Solidus), °C 1390
1400
Specific Heat Capacity, J/kg-K 480
480
Thermal Conductivity, W/m-K 16
29
Thermal Expansion, µm/m-K 13
10

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.2
2.7
Electrical Conductivity: Equal Weight (Specific), % IACS 2.5
3.2

Otherwise Unclassified Properties

Base Metal Price, % relative 19
8.5
Density, g/cm3 7.8
7.7
Embodied Carbon, kg CO2/kg material 3.8
2.2
Embodied Energy, MJ/kg 53
30
Embodied Water, L/kg 180
110

Common Calculations

PREN (Pitting Resistance) 38
16
Resilience: Ultimate (Unit Rupture Work), MJ/m3 170
95
Resilience: Unit (Modulus of Resilience), kJ/m3 730
310
Stiffness to Weight: Axial, points 15
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 26
21
Strength to Weight: Bending, points 23
20
Thermal Diffusivity, mm2/s 4.3
7.9
Thermal Shock Resistance, points 20
21

Alloy Composition

Carbon (C), % 0 to 0.030
0.15 to 0.3
Chromium (Cr), % 24.5 to 26.5
13.5 to 15
Copper (Cu), % 0.8 to 1.3
0
Iron (Fe), % 58.4 to 66.6
80.9 to 85.6
Manganese (Mn), % 0 to 2.0
0 to 1.0
Molybdenum (Mo), % 2.5 to 3.5
0.4 to 0.85
Nickel (Ni), % 5.5 to 7.0
0.35 to 0.85
Nitrogen (N), % 0.12 to 0.25
0
Phosphorus (P), % 0 to 0.030
0 to 0.040
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.020
0 to 0.030