EN 1.4518 Stainless Steel vs. S35140 Stainless Steel

Both EN 1.4518 stainless steel and S35140 stainless steel are iron alloys. They have 81% of their average alloy composition in common. There are 31 material properties with values for both materials. Properties with values for just one material (4, in this case) are not shown.

For each property being compared, the top bar is EN 1.4518 stainless steel and the bottom bar is S35140 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 34
34
Fatigue Strength, MPa 160
250
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 79
78
Tensile Strength: Ultimate (UTS), MPa 490
690
Tensile Strength: Yield (Proof), MPa 210
310

Thermal Properties

Latent Heat of Fusion, J/g 300
300
Maximum Temperature: Corrosion, °C 420
500
Maximum Temperature: Mechanical, °C 1000
1100
Melting Completion (Liquidus), °C 1450
1420
Melting Onset (Solidus), °C 1400
1370
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 15
14
Thermal Expansion, µm/m-K 12
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.1
1.7
Electrical Conductivity: Equal Weight (Specific), % IACS 2.4
1.9

Otherwise Unclassified Properties

Base Metal Price, % relative 20
31
Density, g/cm3 7.9
8.0
Embodied Carbon, kg CO2/kg material 4.0
5.5
Embodied Energy, MJ/kg 55
78
Embodied Water, L/kg 160
190

Common Calculations

PREN (Pitting Resistance) 30
28
Resilience: Ultimate (Unit Rupture Work), MJ/m3 140
190
Resilience: Unit (Modulus of Resilience), kJ/m3 100
250
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
24
Strength to Weight: Axial, points 17
24
Strength to Weight: Bending, points 18
22
Thermal Diffusivity, mm2/s 4.1
3.7
Thermal Shock Resistance, points 14
16

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.1
Chromium (Cr), % 18 to 20
20 to 22
Iron (Fe), % 61.4 to 70
44.1 to 52.7
Manganese (Mn), % 0 to 1.5
1.0 to 3.0
Molybdenum (Mo), % 3.0 to 3.5
1.0 to 2.0
Nickel (Ni), % 9.0 to 12
25 to 27
Niobium (Nb), % 0
0.25 to 0.75
Nitrogen (N), % 0
0.080 to 0.2
Phosphorus (P), % 0 to 0.040
0 to 0.045
Silicon (Si), % 0 to 1.5
0 to 0.75
Sulfur (S), % 0 to 0.030
0 to 0.030