EN 1.4530 Stainless Steel vs. N06250 Nickel
EN 1.4530 stainless steel belongs to the iron alloys classification, while N06250 nickel belongs to the nickel alloys. They have a modest 37% of their average alloy composition in common, which, by itself, doesn't mean much. There are 20 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.
For each property being compared, the top bar is EN 1.4530 stainless steel and the bottom bar is N06250 nickel.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 200 | |
| 210 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 76 | |
| 82 |
| Tensile Strength: Ultimate (UTS), MPa | 1030 to 1370 | |
| 710 |
Thermal Properties
| Latent Heat of Fusion, J/g | 270 | |
| 320 |
| Maximum Temperature: Mechanical, °C | 790 | |
| 980 |
| Melting Completion (Liquidus), °C | 1460 | |
| 1490 |
| Melting Onset (Solidus), °C | 1410 | |
| 1440 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 440 |
| Thermal Expansion, µm/m-K | 11 | |
| 13 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 15 | |
| 55 |
| Density, g/cm3 | 7.9 | |
| 8.6 |
| Embodied Carbon, kg CO2/kg material | 3.4 | |
| 10 |
| Embodied Energy, MJ/kg | 46 | |
| 140 |
| Embodied Water, L/kg | 130 | |
| 270 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 14 |
| Stiffness to Weight: Bending, points | 25 | |
| 23 |
| Strength to Weight: Axial, points | 36 to 48 | |
| 23 |
| Strength to Weight: Bending, points | 29 to 35 | |
| 21 |
| Thermal Shock Resistance, points | 35 to 47 | |
| 19 |
Alloy Composition
| Aluminum (Al), % | 0.6 to 0.8 | |
| 0 |
| Carbon (C), % | 0 to 0.015 | |
| 0 to 0.020 |
| Chromium (Cr), % | 11.5 to 12.5 | |
| 20 to 23 |
| Copper (Cu), % | 0 | |
| 0.25 to 1.3 |
| Iron (Fe), % | 74.4 to 77.3 | |
| 7.4 to 19.4 |
| Manganese (Mn), % | 0 to 0.1 | |
| 0 to 1.0 |
| Molybdenum (Mo), % | 1.9 to 2.2 | |
| 10.1 to 12 |
| Nickel (Ni), % | 8.5 to 9.5 | |
| 50 to 54 |
| Nitrogen (N), % | 0 to 0.010 | |
| 0 |
| Phosphorus (P), % | 0 to 0.010 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 to 0.1 | |
| 0 to 0.090 |
| Sulfur (S), % | 0 to 0.0050 | |
| 0 to 0.0050 |
| Titanium (Ti), % | 0.28 to 0.37 | |
| 0 |
| Tungsten (W), % | 0 | |
| 0.25 to 1.3 |