EN 1.4537 Stainless Steel vs. ASTM A182 Grade F92

Both EN 1.4537 stainless steel and ASTM A182 grade F92 are iron alloys. They have 52% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4537 stainless steel and the bottom bar is ASTM A182 grade F92.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 220
240
Elastic (Young's, Tensile) Modulus, GPa 210
190
Elongation at Break, % 42
22
Fatigue Strength, MPa 290
360
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 80
76
Shear Strength, MPa 480
440
Tensile Strength: Ultimate (UTS), MPa 700
690
Tensile Strength: Yield (Proof), MPa 330
500

Thermal Properties

Latent Heat of Fusion, J/g 310
260
Maximum Temperature: Mechanical, °C 1100
590
Melting Completion (Liquidus), °C 1440
1490
Melting Onset (Solidus), °C 1390
1450
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 14
26
Thermal Expansion, µm/m-K 16
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
9.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.3
10

Otherwise Unclassified Properties

Base Metal Price, % relative 34
11
Density, g/cm3 8.1
7.9
Embodied Carbon, kg CO2/kg material 6.1
2.8
Embodied Energy, MJ/kg 84
40
Embodied Water, L/kg 220
89

Common Calculations

PREN (Pitting Resistance) 46
14
Resilience: Ultimate (Unit Rupture Work), MJ/m3 240
140
Resilience: Unit (Modulus of Resilience), kJ/m3 270
650
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 24
24
Strength to Weight: Bending, points 22
22
Thermal Diffusivity, mm2/s 3.7
6.9
Thermal Shock Resistance, points 15
19

Alloy Composition

Aluminum (Al), % 0
0 to 0.020
Boron (B), % 0
0.0010 to 0.0060
Carbon (C), % 0 to 0.020
0.070 to 0.13
Chromium (Cr), % 24 to 26
8.5 to 9.5
Copper (Cu), % 1.0 to 2.0
0
Iron (Fe), % 36.3 to 46.1
85.8 to 89.1
Manganese (Mn), % 0 to 2.0
0.3 to 0.6
Molybdenum (Mo), % 4.7 to 5.7
0.3 to 0.6
Nickel (Ni), % 24 to 27
0 to 0.4
Niobium (Nb), % 0
0.040 to 0.090
Nitrogen (N), % 0.17 to 0.25
0.030 to 0.070
Phosphorus (P), % 0 to 0.030
0 to 0.020
Silicon (Si), % 0 to 0.7
0 to 0.5
Sulfur (S), % 0 to 0.010
0 to 0.010
Titanium (Ti), % 0
0 to 0.010
Tungsten (W), % 0
1.5 to 2.0
Vanadium (V), % 0
0.15 to 0.25
Zirconium (Zr), % 0
0 to 0.010