EN 1.4537 Stainless Steel vs. AWS ENiCrFe-2
EN 1.4537 stainless steel belongs to the iron alloys classification, while AWS ENiCrFe-2 belongs to the nickel alloys. They have 50% of their average alloy composition in common. There are 20 material properties with values for both materials. Properties with values for just one material (14, in this case) are not shown.
For each property being compared, the top bar is EN 1.4537 stainless steel and the bottom bar is AWS ENiCrFe-2.
Metric UnitsUS Customary Units
Mechanical Properties
| Elastic (Young's, Tensile) Modulus, GPa | 210 | |
| 190 |
| Elongation at Break, % | 42 | |
| 28 |
| Poisson's Ratio | 0.28 | |
| 0.3 |
| Shear Modulus, GPa | 80 | |
| 74 |
| Tensile Strength: Ultimate (UTS), MPa | 700 | |
| 790 |
Thermal Properties
| Latent Heat of Fusion, J/g | 310 | |
| 310 |
| Melting Completion (Liquidus), °C | 1440 | |
| 1390 |
| Melting Onset (Solidus), °C | 1390 | |
| 1350 |
| Specific Heat Capacity, J/kg-K | 470 | |
| 450 |
| Thermal Expansion, µm/m-K | 16 | |
| 12 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 34 | |
| 65 |
| Density, g/cm3 | 8.1 | |
| 8.5 |
| Embodied Carbon, kg CO2/kg material | 6.1 | |
| 11 |
| Embodied Energy, MJ/kg | 84 | |
| 160 |
| Embodied Water, L/kg | 220 | |
| 260 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 24 | |
| 23 |
| Strength to Weight: Axial, points | 24 | |
| 26 |
| Strength to Weight: Bending, points | 22 | |
| 22 |
| Thermal Shock Resistance, points | 15 | |
| 24 |
Alloy Composition
| Carbon (C), % | 0 to 0.020 | |
| 0 to 0.1 |
| Chromium (Cr), % | 24 to 26 | |
| 13 to 17 |
| Cobalt (Co), % | 0 | |
| 0 to 0.12 |
| Copper (Cu), % | 1.0 to 2.0 | |
| 0 to 0.5 |
| Iron (Fe), % | 36.3 to 46.1 | |
| 0 to 12 |
| Manganese (Mn), % | 0 to 2.0 | |
| 1.0 to 3.5 |
| Molybdenum (Mo), % | 4.7 to 5.7 | |
| 0.5 to 2.5 |
| Nickel (Ni), % | 24 to 27 | |
| 62 to 85 |
| Niobium (Nb), % | 0 | |
| 0.5 to 4.0 |
| Nitrogen (N), % | 0.17 to 0.25 | |
| 0 |
| Phosphorus (P), % | 0 to 0.030 | |
| 0 to 0.030 |
| Silicon (Si), % | 0 to 0.7 | |
| 0 to 0.75 |
| Sulfur (S), % | 0 to 0.010 | |
| 0 to 0.020 |
| Residuals, % | 0 | |
| 0 to 0.5 |