EN 1.4537 Stainless Steel vs. EN-MC65210 Magnesium

EN 1.4537 stainless steel belongs to the iron alloys classification, while EN-MC65210 magnesium belongs to the magnesium alloys. There are 29 material properties with values for both materials. Properties with values for just one material (5, in this case) are not shown. Please note that the two materials have significantly dissimilar densities. This means that additional care is required when interpreting the data, because some material properties are based on units of mass, while others are based on units of area or volume.

For each property being compared, the top bar is EN 1.4537 stainless steel and the bottom bar is EN-MC65210 magnesium.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 220
80
Elastic (Young's, Tensile) Modulus, GPa 210
44
Elongation at Break, % 42
2.8
Fatigue Strength, MPa 290
110
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 80
17
Shear Strength, MPa 480
150
Tensile Strength: Ultimate (UTS), MPa 700
270
Tensile Strength: Yield (Proof), MPa 330
200

Thermal Properties

Latent Heat of Fusion, J/g 310
340
Maximum Temperature: Mechanical, °C 1100
170
Melting Completion (Liquidus), °C 1440
610
Melting Onset (Solidus), °C 1390
540
Specific Heat Capacity, J/kg-K 470
970
Thermal Conductivity, W/m-K 14
110
Thermal Expansion, µm/m-K 16
26

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
25
Electrical Conductivity: Equal Weight (Specific), % IACS 2.3
110

Otherwise Unclassified Properties

Density, g/cm3 8.1
2.0
Embodied Carbon, kg CO2/kg material 6.1
27
Embodied Energy, MJ/kg 84
220

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 240
6.9
Resilience: Unit (Modulus of Resilience), kJ/m3 270
450
Stiffness to Weight: Axial, points 14
12
Stiffness to Weight: Bending, points 24
59
Strength to Weight: Axial, points 24
38
Strength to Weight: Bending, points 22
47
Thermal Diffusivity, mm2/s 3.7
58
Thermal Shock Resistance, points 15
17

Alloy Composition

Carbon (C), % 0 to 0.020
0
Chromium (Cr), % 24 to 26
0
Copper (Cu), % 1.0 to 2.0
0 to 0.030
Iron (Fe), % 36.3 to 46.1
0 to 0.010
Magnesium (Mg), % 0
92.6 to 95.6
Manganese (Mn), % 0 to 2.0
0 to 0.15
Molybdenum (Mo), % 4.7 to 5.7
0
Nickel (Ni), % 24 to 27
0 to 0.0050
Nitrogen (N), % 0.17 to 0.25
0
Phosphorus (P), % 0 to 0.030
0
Silicon (Si), % 0 to 0.7
0 to 0.010
Silver (Ag), % 0
2.0 to 3.0
Sulfur (S), % 0 to 0.010
0
Unspecified Rare Earths, % 0
2.0 to 3.0
Zinc (Zn), % 0
0 to 0.2
Zirconium (Zr), % 0
0.4 to 1.0
Residuals, % 0
0 to 0.010