EN 1.4539 Stainless Steel vs. C87600 Bronze

EN 1.4539 stainless steel belongs to the iron alloys classification, while C87600 bronze belongs to the copper alloys. There are 28 material properties with values for both materials. Properties with values for just one material (6, in this case) are not shown.

For each property being compared, the top bar is EN 1.4539 stainless steel and the bottom bar is C87600 bronze.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 200
110
Elongation at Break, % 38
18
Poisson's Ratio 0.28
0.33
Shear Modulus, GPa 79
42
Tensile Strength: Ultimate (UTS), MPa 630
470
Tensile Strength: Yield (Proof), MPa 260
230

Thermal Properties

Latent Heat of Fusion, J/g 300
280
Maximum Temperature: Mechanical, °C 1100
190
Melting Completion (Liquidus), °C 1440
970
Melting Onset (Solidus), °C 1390
860
Specific Heat Capacity, J/kg-K 460
410
Thermal Conductivity, W/m-K 12
28
Thermal Expansion, µm/m-K 16
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.7
6.0
Electrical Conductivity: Equal Weight (Specific), % IACS 1.9
6.4

Otherwise Unclassified Properties

Base Metal Price, % relative 31
29
Density, g/cm3 8.1
8.5
Embodied Carbon, kg CO2/kg material 5.7
2.7
Embodied Energy, MJ/kg 78
43
Embodied Water, L/kg 200
300

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 190
71
Resilience: Unit (Modulus of Resilience), kJ/m3 160
240
Stiffness to Weight: Axial, points 14
7.4
Stiffness to Weight: Bending, points 24
19
Strength to Weight: Axial, points 22
16
Strength to Weight: Bending, points 20
16
Thermal Diffusivity, mm2/s 3.2
8.1
Thermal Shock Resistance, points 14
17

Alloy Composition

Carbon (C), % 0 to 0.020
0
Chromium (Cr), % 19 to 21
0
Copper (Cu), % 1.2 to 2.0
88 to 92.5
Iron (Fe), % 43.1 to 51.8
0
Lead (Pb), % 0
0 to 0.5
Manganese (Mn), % 0 to 2.0
0
Molybdenum (Mo), % 4.0 to 5.0
0
Nickel (Ni), % 24 to 26
0
Nitrogen (N), % 0 to 0.15
0
Phosphorus (P), % 0 to 0.030
0
Silicon (Si), % 0 to 0.7
3.5 to 5.5
Sulfur (S), % 0 to 0.010
0
Zinc (Zn), % 0
4.0 to 7.0
Residuals, % 0
0 to 0.5