EN 1.4547 Stainless Steel vs. ASTM A369 Grade FP92

Both EN 1.4547 stainless steel and ASTM A369 grade FP92 are iron alloys. They have 64% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (2, in this case) are not shown.

For each property being compared, the top bar is EN 1.4547 stainless steel and the bottom bar is ASTM A369 grade FP92.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 230
210
Elastic (Young's, Tensile) Modulus, GPa 200
190
Elongation at Break, % 39
19
Fatigue Strength, MPa 290
330
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 80
76
Shear Strength, MPa 510
440
Tensile Strength: Ultimate (UTS), MPa 750
710
Tensile Strength: Yield (Proof), MPa 340
490

Thermal Properties

Latent Heat of Fusion, J/g 300
260
Maximum Temperature: Mechanical, °C 1090
590
Melting Completion (Liquidus), °C 1470
1490
Melting Onset (Solidus), °C 1420
1450
Specific Heat Capacity, J/kg-K 460
470
Thermal Conductivity, W/m-K 14
26
Thermal Expansion, µm/m-K 17
13

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 2.0
9.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.3
10

Otherwise Unclassified Properties

Base Metal Price, % relative 28
11
Density, g/cm3 8.0
7.9
Embodied Carbon, kg CO2/kg material 5.6
2.8
Embodied Energy, MJ/kg 75
40
Embodied Water, L/kg 190
89

Common Calculations

PREN (Pitting Resistance) 45
14
Resilience: Ultimate (Unit Rupture Work), MJ/m3 240
120
Resilience: Unit (Modulus of Resilience), kJ/m3 290
620
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 26
25
Strength to Weight: Bending, points 23
22
Thermal Diffusivity, mm2/s 3.8
6.9
Thermal Shock Resistance, points 16
19

Alloy Composition

Aluminum (Al), % 0
0 to 0.020
Boron (B), % 0
0.0010 to 0.0060
Carbon (C), % 0 to 0.020
0.070 to 0.13
Chromium (Cr), % 19.5 to 20.5
8.5 to 9.5
Copper (Cu), % 0.5 to 1.0
0
Iron (Fe), % 51 to 56.3
85.8 to 89.1
Manganese (Mn), % 0 to 1.0
0.3 to 0.6
Molybdenum (Mo), % 6.0 to 7.0
0.3 to 0.6
Nickel (Ni), % 17.5 to 18.5
0 to 0.4
Niobium (Nb), % 0
0.040 to 0.090
Nitrogen (N), % 0.18 to 0.25
0.030 to 0.070
Phosphorus (P), % 0 to 0.030
0 to 0.020
Silicon (Si), % 0 to 0.7
0 to 0.5
Sulfur (S), % 0 to 0.010
0 to 0.010
Titanium (Ti), % 0
0 to 0.010
Tungsten (W), % 0
1.5 to 2.0
Vanadium (V), % 0
0.15 to 0.25
Zirconium (Zr), % 0
0 to 0.010