EN 1.4552 Stainless Steel vs. Nickel 684

EN 1.4552 stainless steel belongs to the iron alloys classification, while nickel 684 belongs to the nickel alloys. They have a modest 31% of their average alloy composition in common, which, by itself, doesn't mean much. There are 26 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.

For each property being compared, the top bar is EN 1.4552 stainless steel and the bottom bar is nickel 684.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 150
310
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 29
11
Fatigue Strength, MPa 150
390
Poisson's Ratio 0.28
0.29
Shear Modulus, GPa 77
76
Tensile Strength: Ultimate (UTS), MPa 510
1190
Tensile Strength: Yield (Proof), MPa 200
800

Thermal Properties

Latent Heat of Fusion, J/g 290
320
Maximum Temperature: Mechanical, °C 960
1000
Melting Completion (Liquidus), °C 1430
1370
Melting Onset (Solidus), °C 1380
1320
Specific Heat Capacity, J/kg-K 480
470
Thermal Expansion, µm/m-K 17
13

Otherwise Unclassified Properties

Base Metal Price, % relative 19
75
Density, g/cm3 7.8
8.3
Embodied Carbon, kg CO2/kg material 3.6
10
Embodied Energy, MJ/kg 52
140
Embodied Water, L/kg 150
360

Common Calculations

Resilience: Ultimate (Unit Rupture Work), MJ/m3 120
120
Resilience: Unit (Modulus of Resilience), kJ/m3 100
1610
Stiffness to Weight: Axial, points 14
13
Stiffness to Weight: Bending, points 25
23
Strength to Weight: Axial, points 18
40
Strength to Weight: Bending, points 18
30
Thermal Shock Resistance, points 11
34

Alloy Composition

Aluminum (Al), % 0
2.5 to 3.3
Boron (B), % 0
0.0030 to 0.010
Carbon (C), % 0 to 0.070
0 to 0.15
Chromium (Cr), % 18 to 20
15 to 20
Cobalt (Co), % 0
13 to 20
Copper (Cu), % 0
0 to 0.15
Iron (Fe), % 63.9 to 73
0 to 4.0
Manganese (Mn), % 0 to 1.5
0 to 0.75
Molybdenum (Mo), % 0
3.0 to 5.0
Nickel (Ni), % 9.0 to 12
42.7 to 64
Niobium (Nb), % 0 to 1.0
0
Phosphorus (P), % 0 to 0.040
0 to 0.015
Silicon (Si), % 0 to 1.5
0 to 0.75
Sulfur (S), % 0 to 0.030
0 to 0.015
Titanium (Ti), % 0
2.5 to 3.3