EN 1.4557 Stainless Steel vs. S33228 Stainless Steel

Both EN 1.4557 stainless steel and S33228 stainless steel are iron alloys. They have 79% of their average alloy composition in common. There are 28 material properties with values for both materials. Properties with values for just one material (8, in this case) are not shown.

For each property being compared, the top bar is EN 1.4557 stainless steel and the bottom bar is S33228 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Brinell Hardness 160
190
Elastic (Young's, Tensile) Modulus, GPa 200
200
Elongation at Break, % 40
34
Fatigue Strength, MPa 260
170
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 80
79
Tensile Strength: Ultimate (UTS), MPa 560
570
Tensile Strength: Yield (Proof), MPa 300
210

Thermal Properties

Latent Heat of Fusion, J/g 300
310
Maximum Temperature: Corrosion, °C 420
560
Maximum Temperature: Mechanical, °C 1090
1100
Melting Completion (Liquidus), °C 1460
1410
Melting Onset (Solidus), °C 1420
1360
Specific Heat Capacity, J/kg-K 460
470
Thermal Expansion, µm/m-K 17
16

Otherwise Unclassified Properties

Base Metal Price, % relative 29
37
Density, g/cm3 8.0
8.0
Embodied Carbon, kg CO2/kg material 5.6
6.2
Embodied Energy, MJ/kg 76
89
Embodied Water, L/kg 190
220

Common Calculations

PREN (Pitting Resistance) 45
27
Resilience: Ultimate (Unit Rupture Work), MJ/m3 190
150
Resilience: Unit (Modulus of Resilience), kJ/m3 210
110
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 24
24
Strength to Weight: Axial, points 19
20
Strength to Weight: Bending, points 19
19
Thermal Shock Resistance, points 12
13

Alloy Composition

Aluminum (Al), % 0
0 to 0.025
Carbon (C), % 0 to 0.020
0.040 to 0.080
Cerium (Ce), % 0
0.050 to 0.1
Chromium (Cr), % 19.5 to 20.5
26 to 28
Copper (Cu), % 0.5 to 1.0
0
Iron (Fe), % 49.5 to 56.3
36.5 to 42.3
Manganese (Mn), % 0 to 1.2
0 to 1.0
Molybdenum (Mo), % 6.0 to 7.0
0
Nickel (Ni), % 17.5 to 19.5
31 to 33
Niobium (Nb), % 0
0.6 to 1.0
Nitrogen (N), % 0.18 to 0.24
0
Phosphorus (P), % 0 to 0.030
0 to 0.020
Silicon (Si), % 0 to 1.0
0 to 0.3
Sulfur (S), % 0 to 0.010
0 to 0.015