EN 1.4565 Stainless Steel vs. AISI 305 Stainless Steel

Both EN 1.4565 stainless steel and AISI 305 stainless steel are iron alloys. They have 77% of their average alloy composition in common. There are 32 material properties with values for both materials. Properties with values for just one material (3, in this case) are not shown.

For each property being compared, the top bar is EN 1.4565 stainless steel and the bottom bar is AISI 305 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
200
Elongation at Break, % 35
34 to 45
Fatigue Strength, MPa 380
210 to 280
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 81
77
Shear Strength, MPa 590
400 to 470
Tensile Strength: Ultimate (UTS), MPa 880
580 to 710
Tensile Strength: Yield (Proof), MPa 480
230 to 350

Thermal Properties

Latent Heat of Fusion, J/g 310
290
Maximum Temperature: Corrosion, °C 460
410
Maximum Temperature: Mechanical, °C 1100
540
Melting Completion (Liquidus), °C 1420
1450
Melting Onset (Solidus), °C 1380
1400
Specific Heat Capacity, J/kg-K 470
480
Thermal Conductivity, W/m-K 12
16
Thermal Expansion, µm/m-K 15
17

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.9
2.4
Electrical Conductivity: Equal Weight (Specific), % IACS 2.1
2.7

Otherwise Unclassified Properties

Base Metal Price, % relative 28
16
Density, g/cm3 7.9
7.8
Embodied Carbon, kg CO2/kg material 5.4
3.2
Embodied Energy, MJ/kg 74
45
Embodied Water, L/kg 210
150

Common Calculations

PREN (Pitting Resistance) 47
18
Resilience: Ultimate (Unit Rupture Work), MJ/m3 260
200 to 210
Resilience: Unit (Modulus of Resilience), kJ/m3 550
130 to 320
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 31
20 to 25
Strength to Weight: Bending, points 26
20 to 23
Thermal Diffusivity, mm2/s 3.2
4.2
Thermal Shock Resistance, points 21
13 to 15

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.12
Chromium (Cr), % 24 to 26
17 to 19
Iron (Fe), % 41.2 to 50.7
65.1 to 72.5
Manganese (Mn), % 5.0 to 7.0
0 to 2.0
Molybdenum (Mo), % 4.0 to 5.0
0
Nickel (Ni), % 16 to 19
10.5 to 13
Niobium (Nb), % 0 to 0.15
0
Nitrogen (N), % 0.3 to 0.6
0
Phosphorus (P), % 0 to 0.030
0 to 0.045
Silicon (Si), % 0 to 1.0
0 to 0.75
Sulfur (S), % 0 to 0.015
0 to 0.030