EN 1.4565 Stainless Steel vs. EN 1.4449 Stainless Steel

Both EN 1.4565 stainless steel and EN 1.4449 stainless steel are iron alloys. Both are furnished in the solution annealed (AT) condition. They have 80% of their average alloy composition in common. There are 33 material properties with values for both materials. Properties with values for just one material (1, in this case) are not shown.

For each property being compared, the top bar is EN 1.4565 stainless steel and the bottom bar is EN 1.4449 stainless steel.

Metric UnitsUS Customary Units

Mechanical Properties

Elastic (Young's, Tensile) Modulus, GPa 210
200
Elongation at Break, % 35
48
Fatigue Strength, MPa 380
240
Impact Strength: V-Notched Charpy, J 110
91
Poisson's Ratio 0.28
0.28
Shear Modulus, GPa 81
78
Shear Strength, MPa 590
440
Tensile Strength: Ultimate (UTS), MPa 880
620
Tensile Strength: Yield (Proof), MPa 480
250

Thermal Properties

Latent Heat of Fusion, J/g 310
290
Maximum Temperature: Corrosion, °C 460
410
Maximum Temperature: Mechanical, °C 1100
960
Melting Completion (Liquidus), °C 1420
1440
Melting Onset (Solidus), °C 1380
1400
Specific Heat Capacity, J/kg-K 470
470
Thermal Conductivity, W/m-K 12
15
Thermal Expansion, µm/m-K 15
16

Electrical Properties

Electrical Conductivity: Equal Volume, % IACS 1.9
2.3
Electrical Conductivity: Equal Weight (Specific), % IACS 2.1
2.6

Otherwise Unclassified Properties

Base Metal Price, % relative 28
19
Density, g/cm3 7.9
7.9
Embodied Carbon, kg CO2/kg material 5.4
3.9
Embodied Energy, MJ/kg 74
54
Embodied Water, L/kg 210
150

Common Calculations

PREN (Pitting Resistance) 47
27
Resilience: Ultimate (Unit Rupture Work), MJ/m3 260
240
Resilience: Unit (Modulus of Resilience), kJ/m3 550
160
Stiffness to Weight: Axial, points 14
14
Stiffness to Weight: Bending, points 25
25
Strength to Weight: Axial, points 31
22
Strength to Weight: Bending, points 26
20
Thermal Diffusivity, mm2/s 3.2
4.0
Thermal Shock Resistance, points 21
14

Alloy Composition

Carbon (C), % 0 to 0.030
0 to 0.035
Chromium (Cr), % 24 to 26
17 to 18.2
Copper (Cu), % 0
0 to 1.0
Iron (Fe), % 41.2 to 50.7
62.4 to 69.3
Manganese (Mn), % 5.0 to 7.0
0 to 2.0
Molybdenum (Mo), % 4.0 to 5.0
2.3 to 2.8
Nickel (Ni), % 16 to 19
11.5 to 12.5
Niobium (Nb), % 0 to 0.15
0
Nitrogen (N), % 0.3 to 0.6
0 to 0.080
Phosphorus (P), % 0 to 0.030
0 to 0.045
Silicon (Si), % 0 to 1.0
0 to 1.0
Sulfur (S), % 0 to 0.015
0 to 0.015