EN 1.4567 Stainless Steel vs. EN 1.4477 Stainless Steel
Both EN 1.4567 stainless steel and EN 1.4477 stainless steel are iron alloys. They have 86% of their average alloy composition in common.
For each property being compared, the top bar is EN 1.4567 stainless steel and the bottom bar is EN 1.4477 stainless steel.
Metric UnitsUS Customary Units
Mechanical Properties
Brinell Hardness | 190 to 240 | |
270 |
Elastic (Young's, Tensile) Modulus, GPa | 190 | |
210 |
Elongation at Break, % | 22 to 51 | |
22 to 23 |
Fatigue Strength, MPa | 190 to 260 | |
420 to 490 |
Impact Strength: V-Notched Charpy, J | 91 to 110 | |
110 |
Poisson's Ratio | 0.28 | |
0.27 |
Shear Modulus, GPa | 76 | |
81 |
Shear Strength, MPa | 390 to 490 | |
550 to 580 |
Tensile Strength: Ultimate (UTS), MPa | 550 to 780 | |
880 to 930 |
Tensile Strength: Yield (Proof), MPa | 200 to 390 | |
620 to 730 |
Thermal Properties
Latent Heat of Fusion, J/g | 290 | |
300 |
Maximum Temperature: Corrosion, °C | 420 | |
460 |
Maximum Temperature: Mechanical, °C | 930 | |
1100 |
Melting Completion (Liquidus), °C | 1410 | |
1430 |
Melting Onset (Solidus), °C | 1370 | |
1380 |
Specific Heat Capacity, J/kg-K | 480 | |
480 |
Thermal Conductivity, W/m-K | 11 | |
13 |
Thermal Expansion, µm/m-K | 17 | |
13 |
Electrical Properties
Electrical Conductivity: Equal Volume, % IACS | 2.4 | |
2.2 |
Electrical Conductivity: Equal Weight (Specific), % IACS | 2.7 | |
2.5 |
Otherwise Unclassified Properties
Base Metal Price, % relative | 16 | |
20 |
Density, g/cm3 | 7.8 | |
7.7 |
Embodied Carbon, kg CO2/kg material | 3.1 | |
3.7 |
Embodied Energy, MJ/kg | 43 | |
52 |
Embodied Water, L/kg | 150 | |
190 |
Common Calculations
PREN (Pitting Resistance) | 19 | |
41 |
Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 150 to 220 | |
180 to 190 |
Resilience: Unit (Modulus of Resilience), kJ/m3 | 100 to 400 | |
940 to 1290 |
Stiffness to Weight: Axial, points | 14 | |
15 |
Stiffness to Weight: Bending, points | 25 | |
25 |
Strength to Weight: Axial, points | 19 to 27 | |
31 to 33 |
Strength to Weight: Bending, points | 19 to 24 | |
26 to 27 |
Thermal Diffusivity, mm2/s | 3.0 | |
3.5 |
Thermal Shock Resistance, points | 12 to 17 | |
23 to 25 |
Alloy Composition
Carbon (C), % | 0 to 0.040 | |
0 to 0.030 |
Chromium (Cr), % | 17 to 19 | |
28 to 30 |
Copper (Cu), % | 3.0 to 4.0 | |
0 to 0.8 |
Iron (Fe), % | 63.3 to 71.5 | |
56.6 to 63.6 |
Manganese (Mn), % | 0 to 2.0 | |
0.8 to 1.5 |
Molybdenum (Mo), % | 0 | |
1.5 to 2.6 |
Nickel (Ni), % | 8.5 to 10.5 | |
5.8 to 7.5 |
Nitrogen (N), % | 0 to 0.1 | |
0.3 to 0.4 |
Phosphorus (P), % | 0 to 0.045 | |
0 to 0.030 |
Silicon (Si), % | 0 to 1.0 | |
0 to 0.5 |
Sulfur (S), % | 0 to 0.015 | |
0 to 0.015 |