EN 1.4567 Stainless Steel vs. EN 1.7160 Steel
Both EN 1.4567 stainless steel and EN 1.7160 steel are iron alloys. They have 70% of their average alloy composition in common. There are 25 material properties with values for both materials. Properties with values for just one material (9, in this case) are not shown.
For each property being compared, the top bar is EN 1.4567 stainless steel and the bottom bar is EN 1.7160 steel.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 190 to 240 | |
| 140 to 170 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 190 |
| Poisson's Ratio | 0.28 | |
| 0.29 |
| Shear Modulus, GPa | 76 | |
| 73 |
| Tensile Strength: Ultimate (UTS), MPa | 550 to 780 | |
| 470 to 1390 |
Thermal Properties
| Latent Heat of Fusion, J/g | 290 | |
| 250 |
| Maximum Temperature: Mechanical, °C | 930 | |
| 420 |
| Melting Completion (Liquidus), °C | 1410 | |
| 1460 |
| Melting Onset (Solidus), °C | 1370 | |
| 1420 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 470 |
| Thermal Conductivity, W/m-K | 11 | |
| 45 |
| Thermal Expansion, µm/m-K | 17 | |
| 13 |
Electrical Properties
| Electrical Conductivity: Equal Volume, % IACS | 2.4 | |
| 7.3 |
| Electrical Conductivity: Equal Weight (Specific), % IACS | 2.7 | |
| 8.3 |
Otherwise Unclassified Properties
| Base Metal Price, % relative | 16 | |
| 2.3 |
| Density, g/cm3 | 7.8 | |
| 7.8 |
| Embodied Carbon, kg CO2/kg material | 3.1 | |
| 1.4 |
| Embodied Energy, MJ/kg | 43 | |
| 19 |
| Embodied Water, L/kg | 150 | |
| 51 |
Common Calculations
| Stiffness to Weight: Axial, points | 14 | |
| 13 |
| Stiffness to Weight: Bending, points | 25 | |
| 24 |
| Strength to Weight: Axial, points | 19 to 27 | |
| 17 to 49 |
| Strength to Weight: Bending, points | 19 to 24 | |
| 17 to 35 |
| Thermal Diffusivity, mm2/s | 3.0 | |
| 12 |
| Thermal Shock Resistance, points | 12 to 17 | |
| 14 to 41 |
Alloy Composition
| Boron (B), % | 0 | |
| 0.00080 to 0.0050 |
| Carbon (C), % | 0 to 0.040 | |
| 0.14 to 0.19 |
| Chromium (Cr), % | 17 to 19 | |
| 0.8 to 1.1 |
| Copper (Cu), % | 3.0 to 4.0 | |
| 0 to 0.25 |
| Iron (Fe), % | 63.3 to 71.5 | |
| 96.8 to 98.1 |
| Manganese (Mn), % | 0 to 2.0 | |
| 1.0 to 1.3 |
| Nickel (Ni), % | 8.5 to 10.5 | |
| 0 |
| Nitrogen (N), % | 0 to 0.1 | |
| 0 |
| Phosphorus (P), % | 0 to 0.045 | |
| 0 to 0.025 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 0.3 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 to 0.025 |