EN 1.4567 Stainless Steel vs. Type 4 Niobium
EN 1.4567 stainless steel belongs to the iron alloys classification, while Type 4 niobium belongs to the otherwise unclassified metals. There are 21 material properties with values for both materials. Properties with values for just one material (13, in this case) are not shown.
For each property being compared, the top bar is EN 1.4567 stainless steel and the bottom bar is Type 4 niobium.
Metric UnitsUS Customary Units
Mechanical Properties
| Brinell Hardness | 190 to 240 | |
| 120 |
| Elastic (Young's, Tensile) Modulus, GPa | 190 | |
| 110 |
| Elongation at Break, % | 22 to 51 | |
| 23 |
| Poisson's Ratio | 0.28 | |
| 0.4 |
| Shear Modulus, GPa | 76 | |
| 38 |
| Tensile Strength: Ultimate (UTS), MPa | 550 to 780 | |
| 220 |
| Tensile Strength: Yield (Proof), MPa | 200 to 390 | |
| 140 |
Thermal Properties
| Latent Heat of Fusion, J/g | 290 | |
| 310 |
| Specific Heat Capacity, J/kg-K | 480 | |
| 270 |
| Thermal Conductivity, W/m-K | 11 | |
| 42 |
| Thermal Expansion, µm/m-K | 17 | |
| 7.3 |
Otherwise Unclassified Properties
| Density, g/cm3 | 7.8 | |
| 8.6 |
| Embodied Water, L/kg | 150 | |
| 160 |
Common Calculations
| Resilience: Ultimate (Unit Rupture Work), MJ/m3 | 150 to 220 | |
| 44 |
| Resilience: Unit (Modulus of Resilience), kJ/m3 | 100 to 400 | |
| 93 |
| Stiffness to Weight: Axial, points | 14 | |
| 6.8 |
| Stiffness to Weight: Bending, points | 25 | |
| 18 |
| Strength to Weight: Axial, points | 19 to 27 | |
| 7.2 |
| Strength to Weight: Bending, points | 19 to 24 | |
| 9.5 |
| Thermal Diffusivity, mm2/s | 3.0 | |
| 18 |
| Thermal Shock Resistance, points | 12 to 17 | |
| 21 |
Alloy Composition
| Carbon (C), % | 0 to 0.040 | |
| 0 to 0.010 |
| Chromium (Cr), % | 17 to 19 | |
| 0 |
| Copper (Cu), % | 3.0 to 4.0 | |
| 0 |
| Hafnium (Hf), % | 0 | |
| 0 to 0.020 |
| Hydrogen (H), % | 0 | |
| 0 to 0.0015 |
| Iron (Fe), % | 63.3 to 71.5 | |
| 0 to 0.010 |
| Manganese (Mn), % | 0 to 2.0 | |
| 0 |
| Molybdenum (Mo), % | 0 | |
| 0 to 0.050 |
| Nickel (Ni), % | 8.5 to 10.5 | |
| 0 to 0.0050 |
| Niobium (Nb), % | 0 | |
| 98.1 to 99.2 |
| Nitrogen (N), % | 0 to 0.1 | |
| 0 to 0.010 |
| Oxygen (O), % | 0 | |
| 0 to 0.025 |
| Phosphorus (P), % | 0 to 0.045 | |
| 0 |
| Silicon (Si), % | 0 to 1.0 | |
| 0 to 0.0050 |
| Sulfur (S), % | 0 to 0.015 | |
| 0 |
| Tantalum (Ta), % | 0 | |
| 0 to 0.5 |
| Titanium (Ti), % | 0 | |
| 0 to 0.020 |
| Tungsten (W), % | 0 | |
| 0 to 0.050 |
| Zirconium (Zr), % | 0 | |
| 0.8 to 1.2 |